Method for producing polymer, method for producing organic acid, and organic acid-producing microorganism

ABSTRACT

The present invention provides a method of producing a polymer, which comprises the step of performing a polymerization reaction using, as a starting material, an organic acid obtained by allowing a microorganism or a treated cell thereof to act on an organic raw material, wherein said microorganism has an ability to produce an organic acid and has been modified so as to produce less aromatic carboxylic acid as compared to an unmodified strain.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of U.S. application Ser. No. 14/030,486 filed Sep. 18, 2013, allowed, which is a continuation of International Application PCT/JP2012/056935, filed on Mar. 16, 2012, and designated the U.S., (and claims priority from Japanese Patent Application 2011-061412 which was filed on Mar. 18, 2011), the entire contents of which are incorporated herein by reference.

TECHNICAL FIELD

The present invention relates to a method of producing a high-quality polymer with less coloration, a method of producing an organic acid for obtaining the polymer, an organic acid-producing microorganism used to produce the organic acid.

BACKGROUND ART

Biodegradable plastic materials, which are eventually decomposed into water and carbon dioxide by microorganisms, are used in a wide variety of applications such as food containers and agricultural materials.

At present, such polyesters are produced by polycondensation of a material derived from a fossil fuel resource; however, in view of recent environmental problems at a global scale such as concerns for depletion of fossil fuel resources and increase in the atmospheric carbon dioxide level, attention has been drawn upon a method of deriving a starting materials of these polymers from a biomass resource.

So far, there have been disclosed technologies for producing a dicarboxylic acid used as a starting material of a polyester, such as succinic acid or adipic acid, from glucose, sucrose or the like of a biomass resource origin by a fermentation method (see Patent Documents 1 and 2 and Non-patent Document 1).

In cases where a dicarboxylic acid is used as a starting material of a polymer, in order to maintain the polymerization activity and to thereby obtain a high-quality polymer with less coloration, a highly pure dicarboxylic acid is required. As a method of purifying a dicarboxylic acid produced by a fermentation method, there are disclosed, for example, a method in which an ion-exchange resin is used and a method in which electrodialysis is used (Patent Documents 3 and 4). Examples of a substance which causes coloration of a polymer include those impurities that exhibit absorption in the ultraviolet region of 250 to 300 nm, and it is described to be useful that such impurities be reduced to not higher than a specific amount (Patent Document 5).

PRIOR ART DOCUMENTS Patent Documents

Patent Document 1: JP 11-113588A

Patent Document 2: JP 11-196888A

Patent Document 3: U.S. Pat. No. 6,284,904

Patent Document 4: JP 2-283289A

Patent Document 5: JP 2010-100617A

Non-Patent Documents

Non-patent Document 1: Journal of the American Chemical Society No. 116 (1994), 399-400

SUMMARY OF THE INVENTION

However, in these production methods described in Patent Documents 1 and 2 and Non-patent Document 1, the resulting acid compound may contain a variety of impurities such as organic acids other than the desired dicarboxylic acid that were produced as by-products, sugars that were left without being completely assimilated by a microorganism, compounds containing elemental nitrogen originated from a biomass resource and metal cations; therefore, a further improvement is necessary.

Furthermore, also in the dicarboxylic acids obtained by the purification processes according to Patent Documents 3 and 4, when the dicarboxylic acids are used as a starting material of a polymer, for example, coloration tends to occur in the resulting polymer; therefore, a further improvement is necessary.

Moreover, in Patent Document 5, the impurities causing coloration of a polymer were not identified and, from the practical standpoint, it is an important problem to attain removal of such impurities from a dicarboxylic acid by a more efficient and inexpensive method.

In view of the above, objects of the present invention are: to provide a method of producing a high-quality polymer with less coloration; to provide a method of producing an organic acid suitable for this purpose; and to provide a microorganism used to produce the organic acid.

In order to solve the above-described problems, the present inventors intensively studied and discovered that, among a variety of impurities that may be contained in an organic acid used as a starting material of a polymer, aromatic carboxylic acids such as protocatechuic acid are the substances that cause coloration of a polymer; and that aromatic carboxylic acids such as protocatechuic acid are not easily separated by purification. Furthermore, the present inventors produced an organic acid by allowing a microorganism modified so that the production of aromatic carboxylic acid such as protocatechuic acid is reduced, or a treated cell thereof, to act on an organic raw material and discovered that, by using such an organic acid to synthesize a polymer, coloration in the resulting polymer can be reduced, there by completed the present invention.

That is, according to the present invention, the following inventions are provided.

-   [1] A method of producing a polymer, which comprises the step of     performing a polymerization reaction using, as a starting material,     an organic acid obtained by allowing a microorganism or a treated     cell of thereof to act on an organic raw material, wherein said     microorganism has an ability to produce the organic acid and has     been modified so as to produce less aromatic carboxylic acid as     compared to an unmodified strain. -   [2] The method according to [1], wherein said microorganism has been     modified so that at least one enzyme activity selected from the     group consisting of DAHP synthase activity, dehydroquinate synthase     activity, dehydroquinate dehydratase activity and dehydroshikimate     dehydratase activity is reduced as compared to an unmodified strain,     and production of an aromatic carboxylic acid is thereby reduced. -   [3] The method according to [1] or [2], wherein said organic acid is     subjected to a crystallization treatment. -   [4] The method according to any one of [1] to [3], wherein said     aromatic carboxylic acid is a hydroxybenzene carboxylic acid. -   [5] The method according to any one of [1] to [4], wherein said     organic acid is succinic acid. -   [6] The method according to [5], wherein said polymer is a polyester     or a polyamide. -   [7] A method of producing an organic acid, comprising the step of     allowing a microorganism or a treated cell thereof to act on an     organic raw material, wherein said microorganism has an ability to     produce the organic acid and has been modified so as to produce less     aromatic carboxylic acid as compared to an unmodified strain. -   [8] The method according to [7], wherein said microorganism has been     modified so that at least one enzyme activity selected from the     group consisting of DAHP synthase activity, dehydroquinate synthase     activity, dehydroquinate dehydratase activity and dehydroshikimate     dehydratase activity is reduced as compared to an unmodified strain,     and production of an aromatic carboxylic acid is thereby reduced. -   [9] The method according to [7] or [8], wherein said microorganism     or a treated cell thereof is allowed to act on said organic raw     material in an anaerobic atmosphere. -   [10] The method according to any one of [7] to [9], wherein said     organic acid is succinic acid. -   [11] The method according to any one of [7] to [10], further     comprising the step of performing a crystallization treatment of     said organic acid. -   [12] The method according to any one of [7] to [11], wherein said     aromatic carboxylic acid is a hydroxybenzene carboxylic acid. -   [13] The method according to any one of [7] to [12], wherein said     microorganism is at least one bacterium selected from the group     consisting of coryneform bacteria, bacteria belonging to the genus     Mycobacterium, bacteria belonging to the genus Rhodococcus, bacteria     belonging to the genus Nocardia and bacteria belonging to the genus     Streptomyces. -   [14] A coryneform bacterium, which has an ability to produce an     organic acid and has been modified so that at least one enzyme     activity selected from the group consisting of dehydroquinate     synthase activity, dehydroquinate dehydratase activity and     dehydroshikimate dehydratase activity is reduced as compared to an     unmodified strain, and the production of an aromatic carboxylic acid     is thereby reduced. -   [15] The coryneform bacterium according to [14], which has been     modified so that the dehydroshikimate dehydratase activity is     reduced. -   [16] The coryneform bacterium according to [15], wherein said     dehydroshikimate dehydratase activity is reduced by disrupting a     gene encoding dehydroshikimate dehydratase or by introducing a     mutation into said gene. -   [17] The coryneform bacterium according to [16], wherein said gene     encoding dehydroshikimate dehydratase is a DNA comprising the     nucleotide sequence shown in SEQ ID NO:15 or a DNA which hybridizes     with a complementary sequence of said nucleotide sequence shown in     SEQ ID NO:15 under stringent conditions and encodes a protein having     dehydroshikimate dehydratase activity. -   [18] The coryneform bacterium according to any one of [14] to [17],     wherein said aromatic carboxylic acid is a hydroxybenzene carboxylic     acid. -   [19] The coryneform bacterium according to [18], wherein said     aromatic carboxylic acid is protocatechuic acid.

By the present invention, production of aromatic carboxylic acids which cause coloration of a polymer can be reduced, so that, by using the organic acid of the present invention as a starting material of a polymer, a high-quality polymer with less coloration can be obtained. By the present invention, the purification step of an organic acid can be simplified and the production cost can thus be reduced. Furthermore, the present invention can greatly contribute to solving the environmental problems and problems of depletion in fossil fuel resources and the like.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram showing the synthetic pathway of protocatechuic acid.

FIG. 2 is a diagram illustrating the procedures for constructing a plasmid pMJPC17.2. The underlined numbers indicate the primers having the sequence shown in the corresponding SEQ ID NOs.

FIG. 3 is a diagram illustrating the procedures for constructing a plasmid pQsuB1.

FIG. 4 is a drawing of a crystallization apparatus.

EMBODIMENTS FOR CARRYING OUT THE INVENTION

The embodiments of the present invention will now be described in detail.

<Microorganism of the Present Invention>

The microorganism according to the present invention has an ability to produce an organic acid and has been modified so as to produce less aromatic carboxylic acid as compared to an unmodified strain. The expression “modified so as to produce less aromatic carboxylic acid as compared to an unmodified strain” encompasses a condition in which the activity of an enzyme relating to a biosynthetic pathway of an aromatic carboxylic acid is directly and indirectly reduced as compared to an unmodified strain; a condition in which, because of an increase in the activity of an enzyme of other biosynthetic pathway which shares a precursor with an aromatic carboxylic acid but branches from the biosynthetic pathway thereof, the flow of the precursor of the aromatic carboxylic acid to its biosynthetic pathway is reduced, so that the biosynthesis of the aromatic carboxylic acid is indirectly reduced; and a condition in which the activity of an enzyme relating to a decomposition pathway of an aromatic carboxylic acid is directly and indirectly increased as compared to an unmodified strain.

Specific examples of such microorganism include those which have been modified so that at least one enzyme activity selected from the group consisting of DAHP synthase activity, dehydroquinate synthase activity, dehydroquinate dehydratase activity and dehydroshikimate dehydratase activity is reduced as compared to an unmodified strain. Thereamong, the microorganism of the present invention is preferably a microorganism which has been modified so that at least one enzyme activity selected from the group consisting of dehydroquinate synthase activity, dehydroquinate dehydratase activity and dehydroshikimate dehydratase activity is reduced as compared to an unmodified strain, more preferably a microorganism which has been modified so that dehydroquinate dehydratase activity and/or dehydroshikimate dehydratase activity is/are reduced as compared to an unmodified strain, particularly preferably a microorganism which has been modified so that dehydroshikimate dehydratase activity is reduced as compared to an unmodified strain.

The term “having an ability to produce an organic acid” used herein means that, when the microorganism is cultured in a medium, the microorganism can produce and accumulate an organic acid in the medium.

The organic acid is not particularly restricted as long as it is an organic acid which is not an aromatic carboxylic acid, and it is preferably an amino acid or a carboxylic acid, more preferably a carboxylic acid, still more preferably an aliphatic carboxylic acid. Further, among these carboxylic acids, the organic acid is preferably a polycarboxylic acid, more preferably a dicarboxylic acid.

Examples of the organic acid which is not an aromatic carboxylic acid include lactic acid, succinic acid, malic acid, fumaric acid, oxaloacetic acid, citric acid, isocitric acid, 2-oxoglutaric acid, cis-aconitic acid, pyruvic acid, acetic acid and amino acids. Thereamong, the organic acid which is not an aromatic carboxylic acid is preferably a dicarboxylic acid, more preferably succinic acid, malic acid, fumaric acid, citric acid, isocitric acid, 2-oxoglutaric acid, cis-aconitic acid or pyruvic acid, still more preferably succinic acid, malic acid or fumaric acid, particularly preferably succinic acid.

Further, the term “an ability to produce an aromatic carboxylic acid” used herein refers to an ability of the microorganism of the present invention to produce and accumulate an aromatic carboxylic acid in a medium when the microorganism is cultured in the medium. The expression “a reduced ability to produce an aromatic carboxylic acid” means that the ability to produce an aromatic carboxylic acid is reduced as compared to an unmodified strain such as a wild-type strain. Here, the term “unmodified strain” encompasses wild-type strains and those strains which have an ability to produce an aromatic carboxylic acid at a level comparable to a wild-type strain, as well as those strains having DAHP synthase activity, dehydroquinate synthase activity, dehydroquinate dehydratase activity and dehydroshikimate dehydratase activity.

Examples of an aromatic carboxylic acid to be reduced during culturing include oxygen-containing heterocyclic aromatic carboxylic acids, nitrogen-containing heterocyclic aromatic carboxylic acids and benzene-based aromatic carboxylic acids.

Examples of the oxygen-containing heterocyclic aromatic carboxylic acids include those in which a carboxyl group is bound, directly or via a linking group, to an oxygen-containing heterocyclic ring having aromatic properties, and specific examples thereof include furan monocarboxylic acids such as furoic acid and pyromucic acid; and furan dicarboxylic acids such dehydromucic acid.

Examples of the nitrogen-containing heterocyclic aromatic carboxylic acids include those in which a carboxyl group is bound, directly or via a linking group, to a nitrogen-containing heterocyclic ring having aromatic properties, and specific examples thereof include pyridine monocarboxylic acids such as nicotinic acid, picolinic acid and isonicotinic acid; and hydroxypyridine carboxylic acids such as citrazinic acid; pyridine dicarboxylic acids such as quinolinic acid, lutidinic acid, isocinchomeronic acid, dipicolinic acid, cinchomeronic acid, dinicotinic acid and uvitonic acid; and pyridine tricarboxylic acids such as berberonic acid.

Examples of the benzene-based aromatic carboxylic acids include those in which a carboxyl group is bound to a benzene ring directly or via a linking group, and the benzene ring has preferably a plurality of substituents, more preferably three or more substituents. Thereamong, hydroxybenzene carboxylic acids having a hydroxyl group in addition to a carboxyl group are preferred and hydroxybenzene carboxylic acids having a plurality of carboxyl groups are more preferred. Further, hydroxybenzene carboxylic acids which have a hydroxy group and a plurality of carboxyl groups at the same time are particularly preferred. These hydroxybenzene carboxylic acids also include derivatives thereof which have a substituent in addition to a hydroxy group and a carboxyl group.

More specific examples of the benzene-based aromatic carboxylic acids include benzene monocarboxylic acids such as benzoic acid, toluic acid, xylic acid, α-toluic acid, cinnamic acid and hydrocinnamic acid; benzene dicarboxylic acids such as phthalic acid, isophthalic acid and terephthalic acid; benzene tricarboxylic acids such as hemimellitic acid, trimellitic acid and trimesic acid; hydroxybenzene carboxylic acids such as salicylic acid and creosotic acid; dihydroxybenzene carboxylic acids such as pyrocatechuic acid, protocatechuic acid, resorcylic acid and gentisic acid; and trihydroxybenzene carboxylic acids such as gallic acid.

Thereamong, it is preferred that a furan dicarboxylic acid such as dehydromucic acid; a hydroxypyridine carboxylic acid such as citrazinic acid; a pyridine dicarboxylic acid such as quinolinic acid, lutidinic acid, isocinchomeronic acid, dipicolinic acid, cinchomeronic acid, dinicotinic acid or uvitonic acid; a pyridine tricarboxylic acid such as berberonic acid; a benzene dicarboxylic acid such as phthalic acid, isophthalic acid or terephthalic acid; a benzene tricarboxylic acid such as hemimellitic acid, trimellitic acid or trimesic acid; a hydroxybenzene carboxylic acid such as salicylic acid or creosotic acid; a dihydroxybenzene carboxylic acid such as pyrocatechuic acid, protocatechuic acid, resorcylic acid or gentisic acid; or a trihydroxybenzene carboxylic acid such as gallic acid be reduced.

It is more preferred that a hydroxypyridine carboxylic acid such as citrazinic acid; a pyridine dicarboxylic acid such as quinolinic acid, lutidinic acid, isocinchomeronic acid, dipicolinic acid, cinchomeronic acid, dinicotinic acid or uvitonic acid; a benzene dicarboxylic acid such as phthalic acid, isophthalic acid or terephthalic acid; a benzene tricarboxylic acid such as hemimellitic acid, trimellitic acid or trimesic acid; a hydroxybenzene carboxylic acid such as salicylic acid or creosotic acid; or a dihydroxybenzene carboxylic acid such as pyrocatechuic acid, protocatechuic acid, resorcylic acid or gentisic acid be reduced.

It is still more preferred that a pyridine dicarboxylic acid such as quinolinic acid, lutidinic acid, isocinchomeronic acid, dipicolinic acid, cinchomeronic acid, dinicotinic acid or uvitonic acid; a hydroxybenzene carboxylic acid such as salicylic acid or creosotic acid; or a dihydroxybenzene carboxylic acid such as pyrocatechuic acid, protocatechuic acid, resorcylic acid or gentisic acid be reduced.

It is especially preferred that lutidinic acid, uvitonic acid, pyrocatechuic acid, protocatechuic acid, resorcylic acid or gentisic acid be reduced.

It is yet still more preferred that pyrocatechuic acid, protocatechuic acid, resorcylic acid or gentisic acid be reduced, and it is particularly preferred that protocatechuic acid be reduced.

Although the details of the mechanism are not clear, causes of coloration are speculated to be that, during the later-described polymer polymerization reaction, these aromatic carboxylic acids are cross-linked between the resulting polymers, or colored substances, in which these aromatic carboxylic acids are configured on a catalyst used in the polymer synthesis, are generated. Therefore, it is preferred that such coloration-causing aromatic carboxylic acid be reduced in the production of an organic acid since it allows the later-described purification process to be simplified and consequently, the production cost of an organic acid can be reduced.

The concentration of an aromatic carboxylic acid in the later-described culture medium or the resulting organic acid can be determined by measuring and analyzing the organic acid by conventionally known column chromatography.

The microorganism according to the present invention may be a microorganism which is obtained by modifying a microorganism intrinsically having an ability to produce an organic acid, or a microorganism imparted with an ability to produce an organic acid by breeding, so that the activity of at least one enzyme selected from the group consisting of DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase and dehydroshikimate dehydratase is reduced and the ability to produce an aromatic carboxylic acid is thereby reduced. Alternatively, the microorganism according to the present invention may also be a microorganism which has been modified as in the above so that the ability to produce an aromatic carboxylic acid is reduced and then imparted with an ability to produce an organic acid.

Examples of a means for imparting an ability to produce an organic acid by breeding include mutation treatments and gene recombination treatments. For each organic acid, a known method, such as enhancement of the expression of the respective biosynthetic enzyme genes, can be employed. For instance, when imparting an ability to produce succinic acid, a means for reducing the lactate dehydrogenase activity by modification, a means for enhancing the pyruvate carboxylate activity or the like may be employed.

The microorganism to be used in the present invention can be obtained by using a microorganism shown below as a parent strain and modifying the parent strain. The type of the parent strain is not particularly restricted as long as it is a microorganism capable of producing an organic acid and examples thereof include coryneform bacteria and those bacteria belonging to the genera Mycobacterium, Rhodococcus, Nocardia and Streptomyces; however, it is more preferably a coryneform bacterium.

The coryneform bacterium is not particularly restricted as long as it is classified into coryneform bacteria, and examples thereof include those bacteria belonging to the genera Corynebacterium, Brevibacterium and Arthrobacter. Among these, those bacteria belonging to the genera Corynebacterium and Brevibacterium are preferred, and more preferred examples include those bacteria classified as Corynebacterium glutamicum, Brevibacterium flavum, Brevibacterium ammoniagenes and Brevibacterium lactofermentum.

Particularly preferred specific examples of the parent strain of the microorganism to be used in the present invention include Brevibacterium flavum MJ-233 (FERM BP-1497), Brevibacterium flavum MJ-233 AB-41 (FERM BP-1498), Brevibacterium ammoniagenes ATCC6872, Corynebacterium glutamicum ATCC31831 and Brevibacterium lactofermentum ATCC13869. It is noted here that, since Brevibacterium flavum may currently be classified as Corynebacterium glutamicum (Lielbl, W., Ehrmann, M., Ludwig, W. and Schleifer, K. H., Int. J. Syst. Bacteriol., 1991, vol. 41, p 255-260), in the present invention, the Brevibacterium flavum MJ-233 strain and its mutant strain, MJ-233 AB-41 strain, are regarded as the same as Corynebacterium glutamicum MJ-233 strain and Corynebacterium glutamicum MJ-233 AB-41 strain, respectively.

Brevibacterium flavum MJ-233 has been deposited as of Apr. 28, 1975, with National Institute of Bioscience and Human Technology, Agency of Industrial Science and Technology, Ministry of International Trade and Industry (currently, International Patent Organism Depositary, National Institute of Advanced Industrial Science and Technology; Tsukuba Central 6, 1-1-1 Higashi, Tsukuba, Ibaraki 305-8566, Japan) under the accession No. FERM P-3068 and converted to an international deposit under the accession No. FERM BP-1497 as of May 1, 1981, under the Budapest Treaty.

Further, the above-described microorganisms to be used as a parent strain may be not only a wild-type strain, but also any of mutant strains obtained by a conventional mutation treatment such as UV irradiation or NTG treatment and recombinant strains induced by a genetic method such as cell fusion or genetic recombination.

In the following descriptions, the aromatic carboxylic acid is assumed to be protocatechuic acid.

Protocatechuic acid is synthesized from 3-dehydrosikimate via the shikimic acid pathway where a condensation reaction between phosphoenolpyruvate, which is an intermediate metabolite of the glycolytic pathway, and erythrose-4-phosphate, which is an intermediate metabolite of the pentose phosphate pathway, is catalyzed by enzymes such as DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase and dehydroshikimate dehydratase. The synthetic pathway of protocatechuic acid is shown in FIG. 1.

The microorganism to be used in the present invention can be obtained by modifying the above-described strain so that at least one enzyme activity selected from the group consisting of DAHP synthase activity, dehydroquinate synthase activity, dehydroquinate dehydratase activity and dehydroshikimate dehydratase activity is reduced as compared to an unmodified strain.

The term “DAHP synthase activity” refers to an activity to catalyze a reaction in which phosphoenolpyruvate and erythrose-4-phosphate are condensed to yield DAHP (3-deoxy-D-arabino-heptulosonate-7-phosphate) (EC: 2.5.1.54). The phrase “modified so that the DAHP synthase activity is reduced” means that the DAHP synthase activity is lower than that of an unmodified strain such as wild-type strain. The DAHP synthase activity is reduced to preferably not higher than 30%, more preferably not higher than 10% per unit cell weight, as compared to that of an unmodified strain. Further, the DAHP synthase activity may also be completely lost. A reduction in the DAHP synthase activity can be verified by measuring the DAHP synthase activity in accordance with a known method such as the one described in Liu, et al. (Liu Y. J., Li P. P., Zhao K. X., Wang B. J., Jiang C. Y., Drake H. L. and Liu S. J., Appl. Environ. Microbiol., 2008, vol. 74(14), p 5497-5503).

The term “dehydroquinate synthase activity” refers to an activity to catalyze a reaction in which 3-dehydroquinate is produced from DAHP (3-deoxy-D-arabino-heptulosonate-7-phosphate) (EC: 4.2.3.4). The phrase “modified so that the dehydroquinate synthase activity is reduced” means that the dehydroquinate synthase activity is lower than that of an unmodified strain such as wild-type strain. The dehydroquinate synthase activity is reduced to preferably not higher than 30%, more preferably not higher than 10% per unit cell weight, as compared to that of an unmodified strain. Further, the dehydroquinate synthase activity may also be completely lost. A reduction in the dehydroquinate synthase activity can be verified by measuring the dehydroquinate synthase activity in accordance with a known method such as the one described in de Mendonca, et al. (de Mendonca J. D., Ely F., Palma M. S., Frazzon J., Basso L. A. and Santos D. S., J. Bacteriol., 2007, vol. 189(17), p 6246-6252).

The term “dehydroquinate dehydratase activity” refers to an activity to catalyze a reaction in which 3-dehydroshikimate is produced from 3-dehydroquinate (EC: 4.2.1.10). The phrase “modified so that the dehydroquinate dehydratase activity is reduced” means that the dehydroquinate dehydratase activity is lower than that of an unmodified strain such as wild-type strain. The dehydroquinate synthase activity is reduced to preferably not higher than 30%, more preferably not higher than 10% per unit cell weight, as compared to that of an unmodified strain. Further, the dehydroquinate dehydratase activity may also be completely lost. A reduction in the dehydroquinate dehydratase activity can be verified by measuring the dehydroquinate dehydratase activity in accordance with a known method such as the one described in Elsemore, et al. (Elsemore D. A. and Ornston L. N., J. Bacteriol., 1995, vol. 177(20), p 5971-5978).

The term “dehydroshikimate dehydratase activity” refers to an activity to catalyze a reaction in which protocatechuic acid is produced from 3-dehydroshikimate (EC: 4.2.1.-). The phrase “modified so that the dehydroshikimate dehydratase activity is reduced” means that the dehydroshikimate dehydratase activity is lower than that of an unmodified strain such as wild-type strain. The dehydroshikimate dehydratase activity is reduced to preferably not higher than 30%, more preferably not higher than 10% per unit cell weight, as compared to that of an unmodified strain. Further, the dehydroshikimate dehydratase activity may be completely lost as well. A reduction in the dehydroshikimate dehydratase activity can be verified by measuring the dehydroshikimate dehydratase activity in accordance with a known method such as the one described in Elsemore, et al. (Elsemore D. A. and Ornston L. N., J. Bacteriol., 1995, vol. 177(20), p 5971-5978).

A strain which has been modified so that at least one enzyme activity selected from the group consisting of DAHP synthase activity, dehydroquinate synthase activity, dehydroquinate dehydratase activity and dehydroshikimate dehydratase activity is reduced as compared to an unmodified strain can be obtained by treating the above-described parent strain with a mutagenic agent normally used in a mutation treatment, such as N-methyl-N′-nitro-N-nitrosoguanidine (NTG) or nitrous acid, and then selecting a strain in which the enzyme activity of interest is reduced.

Alternatively, such a strain may also be obtained by modifying a parent strain with the genes encoding the respective enzymes. Specifically, this can be achieved by, for example, disrupting a gene on a chromosome or modifying a promoter or an expression control sequence such as Sine-Dalgarno (SD) sequence.

A DAHP synthase gene on a chromosome is not particularly restricted as long as it encodes a protein having DAHP synthase activity, and examples thereof include genes originated from Corynebacterium glutamicum MJ-233 strain which comprises the nucleotide sequence shown in SEQ ID NO:7 or 9 (hereinafter, also referred to as “the aroF gene” and “the aroG gene”, respectively).

Further, a dehydroquinate synthase gene, a dehydroquinate dehydratase gene and a dehydroshikimate dehydratase gene are also not particularly restricted as long as they encode a protein having the respective enzyme activity, and examples thereof include genes originated from Corynebacterium glutamicum MJ-233 strain, each of which comprises the nucleotide sequence shown in SEQ ID NO:11, 13 or 15 (hereinafter, also referred to as “the aroB gene”, “the qsuC gene” and “the qsuB gene”, respectively).

Further, the aroF gene, aroG gene, aroB gene, qsuC gene and qsuB gene may also each be a gene which encodes a protein comprising the amino acid sequence as shown in SEQ ID NO:8, 10, 12, 14 or 16 except that one or several amino acids are substituted, deleted, inserted or added, as long as the resulting protein has the respective enzyme activity. Here, the term “several amino acids” usually means 2 or more, and not more than 20 amino acids, preferably not more than 10 amino acids, more preferably not more than 5 amino acids.

Further, in accordance with the type of the microorganism to be used as a host, it is also possible to use a DAHP synthase gene, a dehydroquinate synthase gene, a dehydroquinate dehydratase gene and a dehydroshikimate dehydratase gene that are originated from a bacterium other than coryneform bacterium or other microorganism. As the DAHP synthase gene, dehydroquinate synthase gene, dehydroquinate dehydratase gene and dehydroshikimate dehydratase gene that are originated from a microorganism, for example, genes whose nucleotide sequences have already been determined or genes encoding a protein having an activity of DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase or dehydroshikimate dehydratase, which are isolated from a chromosome of a microorganism based on the homology or the like to determine the nucleotide sequences thereof, may be used. In addition, once the nucleotide sequences are determined, genes that are synthesized in accordance with the thus determined nucleotide sequences may also be used. These genes can be obtained by amplifying a region containing the respective promoter thereof and an ORF region in accordance with a hybridization method or a PCR method.

A method of disrupting the qsuB gene in a coryneform bacterium will now be described. The qsuB gene can be acquired by, for example, synthesizing a synthetic oligonucleotide based on the above-described sequence and then cloning the thus obtained oligonucleotide by PCR using a chromosomal DNA of Corynebacterium glutamicum as a template. A chromosomal DNA can be prepared from a DNA donor bacterium by, for example, the method of Saito and Miura (see Saito H. and Miura K., Biochim Biophys Acta., 1963, vol. 72, p 619-629; Text for Bioengineering Experiments, edited by the Society for Biotechnology, Japan, p 97-98, Baifukan, 1992).

The qsuB gene prepared in the above-described manner or a part thereof can be used for gene disruption. It is noted here that, since the gene to be disrupted may be any gene as long as it has a homology (identity) at such a level that induces homologous recombination with the qsuB gene on a chromosomal DNA of the bacterium to be disrupted, a gene having a homology to the sequence shown in SEQ ID NO:15 can also be used. Here, the “homology at such a level that induces homologous recombination” is preferably not less than 80%, more preferably not less than 90%, particularly preferably not less than 95%. Further, homologous recombination may occur between any DNAs as long as they can hybridize with the above-described gene (complementary strand of SEQ ID NO:15) under stringent conditions. Here, the stringent conditions may be, for example, those where genes are hybridized under a washing condition of conventional Southern hybridization comprising the salt concentrations equivalent to 1×SSC and 0.1% SDS at 60° C., preferably a condition comprising the salt concentrations equivalent to 0.1×SSC and 0.1% SDS at 60° C.

Further, as the aroF gene, aroG gene, aroB gene and qsuC gene, genes having a homology to the sequences shown in SEQ ID NO:7, 9, 11 and 13 (DNAs which can hybridize with the complementary strands of SEQ ID NO:7, 9, 11 and 13 under stringent conditions) can be used, respectively.

Using the above-described gene, the qsuB gene on a chromosome can be disrupted by, for example, deleting a partial sequence of the qsuB gene to prepare a defective qsuB gene which has been modified not to produce normal QsuB protein; transforming a coryneform bacterium with a DNA containing the gene; and then allowing the gene on the chromosome to undergo recombination with the defective gene. Such gene disruption by gene substitution utilizing homologous recombination has already been established and examples thereof include a method in which a linear DNA is used and a method in which a plasmid containing a temperature-sensitive replication origin is used (U.S. Pat. No. 6,303,383 and JP H05-007491A). Further the above-described gene disruption by gene substitution utilizing homologous recombination can also be performed by using a plasmid which does not have replication capacity in a host. As such a plasmid which does not have replication capacity in a coryneform bacterium, a plasmid having replication capacity in Escherichia coli is preferred, and examples thereof include pHSG299 (manufactured by Takara Bio Inc.) and pHSG399 (manufactured by Takara Bio Inc.). In the above, a case where the qsuB gene is disrupted in a coryneform bacterium was described; however, disruption of the aroF gene, aroG gene, aroB gene or qsuC gene as well as disruption in other bacteria can also be achieved in the same manner as described above.

In order to obtain a microorganism having a reduced ability to produce an aromatic carboxylic acid such as protocatechuic acid, as described in the above, a microorganism modified so that the activity of at least one enzyme selected from the group consisting of DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase and dehydroshikimate dehydratase is reduced may be employed; however, a microorganism which has been modified so that the dehydroshikimate dehydratase activity is reduced is preferably used. The reason therefor is as follows. When the activity of DAHP synthase, dehydroquinate synthase or dehydroquinate dehydratase is reduced, not only the synthesis of protocatechuic acid, but also the synthesis of metabolites such as phenylalanine that are synthesized by the shikimic acid pathway and required for growth become difficult, so that growth tends to be suppressed. In fact, it is reported that the growth of a coryneform bacterium having a disruption in the gene encoding DAHP synthase was inhibited on a synthetic medium (Liu Y. J., Li P. P., Zhao K. X., Wang B. J., Jiang C. Y., Drake H. L., Liu S. J., Appl. Environ. Microbiol., 2008, vol. 74(14), p 5497-5503). Accordingly, in cases where the activities of these enzymes are reduced, it is required to add an aromatic amino acid such as phenylalanine in order to allow the microorganism to grow. Meanwhile, since the shikimic acid pathway is not blocked even when the dehydroshikimate dehydratase activity is reduced, it is believed that such deterioration in growth does not occur. Accordingly, a microorganism which has been modified so that the activity of dehydroshikimate dehydratase is reduced is preferred because the amount of aromatic amino acids such as phenylalanine or organic nitrogen containing an aromatic amino acid that are required to be added for growth may be small and, therefore, such a microorganism can be grown on a simple medium such as synthetic medium, which is economical.

In order to obtain a microorganism having a reduced ability to produce an aromatic carboxylic acid such as protocatechuic acid, as described in the above, either a microorganism which has been modified so that the activity of at least one enzyme selected from the group consisting of DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase and dehydroshikimate dehydratase is reduced or a microorganism which has been modified so that the activity of shikimate dehydrogenase is enhanced may be employed.

The term “shikimate dehydrogenase activity” refers to an activity to catalyze a reaction in which shikimate is produced from 3-dehydroshikimate (EC: 1.1.1.25, 1.1.1.282, 1.1.5.8). The phrase “modified so that the shikimate dehydrogenase activity is enhanced” means that the shikimate dehydrogenase activity is higher than that of an unmodified strain such as wild-type strain. The shikimate dehydrogenase activity is increased to preferably not less than 1.5 times, more preferably not less than 3 times per unit cell weight, as compared to that of an unmodified strain. An enhancement in the shikimate dehydrogenase activity can be verified by measuring the shikimate dehydrogenase activity in accordance with a known method such as the one described in Fonseca, et al. (Fonseca I. O., Magalhaes M. L., Oliveira J. S., Silva R. G., Mendes M. A., Palma M. S., Santos D. S. and Basso L. A., Protein Expr. Purif., 2006, vol. 46(2), p 429-437).

A strain in which the shikimate dehydrogenase activity is enhanced can be obtained by treating a parent strain with a mutagenic agent normally used in a mutation treatment, such as N-methyl-N′-nitro-N-nitrosoguanidine (NTG) or nitrous acid, and then selecting a strain having an increased shikimate dehydrogenase activity.

Alternatively, such a strain may also be obtained by modifying a parent strain with the gene encoding the shikimate dehydrogenase. Specifically, the shikimate dehydrogenase activity can be enhanced by increasing the copy number of the shikimate dehydrogenase gene, and the copy number can be increased by, for example, using a plasmid or increasing the number of copies on a chromosome by a known homologous recombination method. Further, an enhancement of the shikimate dehydrogenase activity can also be achieved by introducing a mutation to a promoter of the shikimate dehydrogenase gene on a chromosome or a plasmid or by allowing the shikimate dehydrogenase gene to be highly expressed by substitution or the like thereof into a stronger promoter.

The shikimate dehydrogenase gene is not particularly restricted as long as it encodes a protein having shikimate dehydrogenase activity, and examples thereof include a gene originated from Corynebacterium glutamicum MJ-233 strain which comprises the nucleotide sequence shown in SEQ ID NO:17 (hereinafter, also referred to as “the qsuD gene”).

Further, the qsuD gene may also be, as long as it encodes a protein having shikimate dehydrogenase activity, a DNA which hybridizes with a DNA having a sequence complementary to the above-described nucleotide sequence under stringent conditions or a homolog such as a DNA which has a homology of not less than 80%, preferably not less than 90%, more preferably not less than 95%, particularly preferably not less than 99% to the above-described nucleotide sequence. Here, the stringent conditions may be, for example, those where genes are hybridized under a washing condition of conventional Southern hybridization comprising the salt concentrations equivalent to 1×SSC and 0.1% SDS at 60° C., preferably a condition comprising the salt concentrations equivalent to 0.1×SSC and 0.1% SDS at 60° C.

Further, the qsuD gene may also be a gene which encodes a protein comprising the amino acid sequence as shown in SEQ ID NO:18 except that one or several amino acids are substituted, deleted, inserted or added, as long as the resulting protein has the shikimate dehydrogenase activity. Here, the term “several amino acids” usually means 2 or more, but not more than 20 amino acids, preferably not more than 10 amino acids, more preferably not more than 5 amino acids.

Further, a shikimate dehydrogenase gene originated from a non-coryneform bacterium, other microorganism, an animal or a plant may also be used. As the shikimate dehydrogenase gene originated from other microorganism, an animal or a plant, for example, a gene whose nucleotide sequence has already been determined or a gene encoding a protein having shikimate dehydrogenase activity which is isolated from a chromosome of a microorganism, an animal or a plant based on the homology or the like to determine the nucleotide sequence thereof, may be used. In addition, once the nucleotide sequence is determined, a gene synthesized in accordance with the thus determined nucleotide sequence may also be used. These genes can be obtained by amplifying a region containing the respective promoter thereof and an ORF region in accordance with a hybridization method or a PCR method.

By inserting the thus isolated gene encoding shikimate dehydrogenase into a known expression vector so that the gene can be expressed, a shikimate dehydrogenase expression vector is provided. By performing transformation with this expression vector, a shikimate dehydrogenase activity-enhanced strain can be obtained. Alternatively, a shikimate dehydrogenase activity-enhanced strain can also be obtained by incorporating a DNA encoding shikimate dehydrogenase into a chromosomal DNA of a host bacterium by homologous recombination or the like so that the incorporated DNA can be expressed. These transformation and homologous recombination can be carried out in accordance with a conventional method known to those skilled in the art.

When introducing a shikimate dehydrogenase gene into a chromosome or a plasmid, an appropriate promoter and more preferably a terminator are incorporated into a 5′-upstream region and a 3′-downstream region of the gene, respectively. These promoter and terminator are not particularly restricted as long as they are known to function in a bacterium to be used as a host, and they may be the promoter and terminator of the shikimate dehydrogenase gene itself or may be replaced with other promoter and terminator. The vectors, promoters, terminators and the like that can be used in a variety of bacteria are described in detail in, for example, “Fundamental Microbiology (Biseibutsugaku Kiso-kouza) 8; Genetic Engineering, Kyoritsu Shuppan Co., Ltd.”.

A method of enhancing the qsuD gene in a coryneform bacterium will now be described. In cases where a coryneform bacterium is used, a recombinant plasmid capable of enhancing the expression of the qsuD gene in the coryneform bacterium can be obtained by introducing a DNA fragment containing the qsuD gene into a plasmid vector which contains a gene regulating the replication and growth functions of a plasmid in the coryneform bacterium. By transforming a coryneform bacterium such as Corynebacterium glutamicum MJ-233 strain with the thus obtained recombinant vector, a coryneform bacterium having an enhanced expression of the qsuD gene can be obtained. This transformation can be carried out by, for example, an electric pulse method (Vertes A. A., Inui M., Kobayashi M., Kurusu Y. and Yukawa H., Res. Microbiol., 1993, vol. 144(3), p 181-185).

A plasmid vector capable of introducing a gene into a coryneform bacterium is not particularly restricted as long as it contains at least a gene which regulates the replication and growth functions in the coryneform bacterium. Specific examples of such plasmid vector include the plasmid pCRY30 described in JP H3-210184A; the plasmids pCRY21, pCRY2KE, pCRY2KX, pCRY31, pCRY3KE and pCRY3KX, which are described in JP H2-72876A and U.S. Pat. No. 5,185,262; the plasmids pCRY2 and pCRY3 which are described in JP H1-191686A; the plasmid pAM330 described in JP S58-67679A; the plasmid pHM1519 described in JP S58-77895A; the plasmids pAJ655, pAJ611 and pAJ1844, which are described in JP S58-192900A; the plasmid pCG1 described in JP S57-134500A; the plasmid pCG2 described in JP S58-35197A; and the plasmids pCG4 and pCG11 which are described in JP S57-183799A. Thereamong, as a plasmid vector to be used in a host-vector system of a coryneform bacterium, a plasmid vector which contains a gene regulating the replication and growth functions of a plasmid in the coryneform bacterium and a gene regulating the function of stabilizing the plasmid in the coryneform bacterium is preferred. For example, the plasmids pCRY30, pCRY21, pCRY2KE, pCRY2KX, pCRY31, pCRY3KE and pCRY3KX can be suitably employed.

In the above-described recombinant plasmid or incorporation into a chromosome, a promoter used to express the qsuD gene may be any promoter as long as it functions in the coryneform bacterium, and it may also be the promoter of the qsuD gene itself. The expression level of the qsuD gene can also be adjusted by appropriately selecting the promoter. In the above, a case where a coryneform bacterium is used was described; however, enhancement of the shikimate dehydrogenase activity in other bacteria can also be achieved in the same manner as described above.

The microorganism according to the present invention may also be a bacterium which is, in addition to being modified so that the ability to produce an aromatic carboxylic acid is reduced (modification by which the activity of at least one enzyme selected from the group consisting of DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase and dehydroshikimate dehydratase is reduced or the shikimate dehydrogenase activity is enhanced), modified so that the lactate dehydrogenase (hereinafter, also referred to as “LDH”) activity is reduced. The term “LDH activity” used herein refers to an activity to catalyze a reaction in which pyruvate is reduced to yield lactate (EC: 1.1.1.27). The phrase “the LDH activity is reduced” means that the LDH activity is lower than that of an unmodified strain. The LDH activity is reduced to preferably not higher than 30%, more preferably not higher than 10% per unit cell weight, as compared to that of an unmodified strain. Further, the LDH activity may also be completely lost. A reduction in the LDH activity can be verified by measuring the LDH activity in accordance with a known method such as the one described in Kanarek, et al. (Kanarek L. and Hill R. L., J. Biol. Chem., 1964, vol. 239, p 4202-4206).

Specific examples of a method for preparing a strain in which the LDH activity is reduced include the method described in JP H11-206385A which utilizes homologous recombination on a chromosome and the method in which the sacB gene is used (Schafer A., Tauch A., Jager W., Kalinowski J., Thierbach G. and Puhler A., Gene, 1994, vol. 145(1), p 69-73). A bacterium in which the LDH activity and the ability to produce an aromatic carboxylic acid are both reduced can be obtained by, for example, preparing a bacterium whose ldh gene is disrupted and then modifying the bacterium so that the ability to produce an aromatic carboxylic acid is reduced. It is noted here, however, that whichever this modification operation for reducing the LDH activity or the modification operation for reducing the ability to produce an aromatic carboxylic acid may be performed first.

Further, the microorganism to be used in the present invention may also be a bacterium which is, in addition to being modified so that the ability to produce an aromatic carboxylic acid is reduced (modification by which the activity of at least one enzyme selected from the group consisting of DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase and dehydroshikimate dehydratase is reduced or the shikimate dehydrogenase activity is enhanced), modified so that the pyruvate carboxylase (hereinafter, also referred to as “PC”) activity is enhanced. The term “PC activity” used herein refers to an activity to catalyze a reaction in which pyruvate is carboxylated to yield oxaloacetate (EC: 6.4.1.1). The phrase “the PC activity is enhanced” means that the PC activity is higher than that of an unmodified strain. The PC activity is increased to preferably not less than 1.5 times, more preferably not less than 3 times per unit bacterial weight, as compared to that of an unmodified strain. An enhancement in the PC activity can be verified by measuring the PC activity in accordance with a known method such as the one described in Fisher, et al. (Fisher S. H. and Magasanik B., J. Bacteriol., 1984, vol. 158(1), p 55-62).

A strain in which the PC activity is enhanced can be prepared in the same manner as the above-described method of enhancing the shikimate dehydrogenase activity. More specifically, such a strain can be prepared by, for example, in the same manner as the method described in JP H11-196888A, introducing a pc gene into a coryneform bacterium to allow the gene to be highly expressed. As a specific pc gene, for example, the pc gene originated from Corynebacterium glutamicum (Peters-Wendisch P. G., Kreutzer C., Kalinowski J., Patek M., Sahm H. and Eikmanns B. J., Microbiology, 1998, vol. 144, p 915-927) may be used. Further, as the pc gene, a DNA which hybridizes with the pc gene originated from Corynebacterium glutamicum under stringent conditions or a DNA encoding a protein having PC activity which has a homology of not less than 80%, preferably not less than 90%, more preferably not less than 95%, particularly preferably not less than 99% to the nucleotide sequence of the pc gene can also be suitably used.

Moreover, a pc gene originated from a coryneform bacterium other than Corynebacterium glutamicum or other microorganism, or an animal/plant-derived pc gene can also be used. Particularly, the sequences of the pc genes originated from the following microorganisms, plants or animals are already known (references are provided below) and these pc genes can be obtained by performing hybridization in the same manner as described in the above or by amplifying the ORF region thereof by PCR.

Human [Biochem. Biophys. Res. Comm., 202, 1009-1014, (1994)]

Mouse [Proc. Natl. Acad. Sci. USA., 90, 1766-1779, (1993)]

Rat [GENE, 165, 331-332, (1995)]

Yeast; Saccharomyces cerevisiae [Mol. Gen. Genet., 229, 307-315, (1991)]

Schizosaccharomyces pombe [DDBJ Accession No. D78170]

Bacillus stearothermophilus [GENE, 191, 47-50, (1997)]

Rhizobium etli [J. Bacteriol., 178, 5960-5970, (1996)]

A bacterium in which the PC activity is enhanced and the ability to produce an aromatic carboxylic acid is reduced can be obtained by, for example, preparing a bacterium in which a pc gene is introduced and highly expressed and then modifying the bacterium so that the ability to produce an aromatic carboxylic acid is reduced. It is noted here, however, that whichever this modification operation for enhancing the PC activity or the modification operation for reducing the ability to produce an aromatic carboxylic acid may be performed first.

Further, the microorganism according to the present invention may also be a bacterium which is, in addition to being modified so that the ability to produce an aromatic carboxylic acid is reduced (modification by which the activity of at least one enzyme selected from the group consisting of DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase and dehydroshikimate dehydratase is reduced or the shikimate dehydrogenase activity is enhanced), modified so that the activity of at least one enzyme selected from the group consisting of acetate kinase (hereinafter, also referred to as “ACK”) and phosphotransacetylase (hereinafter, also referred to as “PTA”) is reduced.

The term “PTA activity” refers to an activity to catalyze a reaction in which phosphate is transferred to acetyl-CoA to yield acetyl phosphate (EC: 2.3.1.8). The phrase “modified so that the PTA activity is reduced” means that the PTA activity is lower than that of an unmodified strain. The PTA activity is reduced to preferably not higher than 30%, more preferably not higher than 10% per unit cell weight, as compared to that of an unmodified strain. Further, the PTA activity may also be completely lost. A reduction in the PTA activity can be verified by measuring the PTA activity in accordance with a known method such as the one described in Klotzsch (Klotzsch H. R., Meth. Enzymol., 1969, vol. 12, p 381-386).

The term “ACK activity” refers to an activity to catalyze a reaction in which acetic acid is produced from acetyl phosphate and ADP (EC: 2.7.2.1). The phrase “modified so that the ACK activity is reduced” means that the ACK activity is lower than that of an unmodified strain. The ACK activity is reduced to preferably not higher than 30%, more preferably not higher than 10% per unit cell weight, as compared to that of an unmodified strain. Further, the ACK activity may be completely lost as well. A reduction in the ACK activity can be verified by measuring the ACK activity in accordance with a known method such as the one described in Ramponi (Ramponi G., Meth. Enzymol., 1975, vol. 42, p 409-426).

The activity of only either one of PTA and ACK may be reduced; however, in order to efficiently reduce the by-production of acetic acid, it is more preferred that the activities of both enzymes be reduced.

It is noted here that, in Corynebacterium glutamicum (including those bacteria classified as Brevibacterium flavum), as described in Microbiology. 1999 February; 145(Pt 2):503-13, since both enzymes of PTA and ACK are encoded by the pta-ack operon (GenBank Accession No. X89084), the activities of both enzymes can be reduced by disrupting the pta gene.

A strain in which the activities of PTA and ACK are reduced can be obtained by disrupting the genes of these enzymes in accordance with a known method such as a method which utilizes homologous recombination or the method in which the sacB gene is used (Schafer A., Tauch A., Jager W., Kalinowski J., Thierbach G. and Puhler A., Gene, 1994, vol. 145(1), p 69-73). Specifically, such a strain can be obtained by the method disclosed in JP 2006-000091A. As the pta gene and the ack gene, in addition the above-described gene having the nucleotide sequence of GenBank Accession No. X89084, a gene having a homology at such a level that induces homologous recombination with the pta gene and the ack gene on the host chromosome can also be used. Here, the “homology at such a level that induces homologous recombination” is preferably not less than 80%, more preferably not less than 90%, particularly preferably not less than 95%. Further, homologous recombination may occur between any DNAs as long as they can hybridize with the above-described genes under stringent conditions.

A bacterium in which the activity of at least one enzyme selected from the group consisting of PTA and ACK as well as the ability to produce an aromatic carboxylic acid are both reduced can be obtained by, for example, preparing a bacterium whose pta gene and ack gene are disrupted and then modifying the bacterium so that the ability to produce an aromatic carboxylic acid is reduced. It is noted here, however, that whichever this modification operation for reducing the activities of PTA and ACK or the modification operation for reducing the ability to produce an aromatic carboxylic acid may be performed first.

Further, the microorganism used in the present invention may also be a bacterium which is obtained by performing two or more of the above-described modifications in combination with the modification for reducing the ability to produce an aromatic carboxylic acid (modification by which the activity of at least one enzyme selected from the group consisting of DAHP synthase, dehydroquinate synthase, dehydroquinate dehydratase and dehydroshikimate dehydratase is reduced or the shikimate dehydrogenase activity is enhanced). When plural modifications are performed, their order is not particularly restricted.

<Method of Producing Organic Acid>

The method of producing an organic acid according to the present invention comprises the step of allowing the above-described microorganism or a treated cell thereof to act on an organic raw material to produce an organic acid. Particularly, it is preferred that an organic acid be produced by allowing the above-described microorganism or a treated cell thereof to act on an organic raw material and then the resulting organic material be recovered.

Examples of the types of organic acids that can be produced and examples of preferred organic acids are as described in the above.

In cases where the above-described microorganism is used in the production of an organic acid, the microorganism may be cultured on a solid slant medium such as an agar medium and then directly used for the reaction; however, it is preferred that the microorganism be cultured in advance in a liquid medium (seed culture) and then used. The medium used for the seed culture may be any conventional medium used for culturing a microorganism. For example, a common culture medium which is prepared by adding natural nutrient sources, such as meat extract, yeast extract and peptone, to a composition composed of inorganic salts such as ammonium sulfate, potassium phosphate and magnesium sulfate can be employed. After the seed culture, it is preferred that the resulting bacterial cells be recovered by centrifugation, membrane separation or the like and then used for the reaction to produce an organic acid. An organic acid may be produced by allowing the seed-cultured microorganism to react with an organic raw material while allowing the microorganism to grow in a medium containing the organic raw material. Alternatively, an organic acid may also be produced by allowing the bacterial cells obtained by culturing in advance to react with an organic raw material in a reaction solution containing the organic raw material.

In the present invention, it is also possible to use a treated cell of a microorganism. Examples of the treated cell include bacterial cells immobilized with acrylamide, carrageenan or the like; a homogenate prepared by pulverizing bacterial cells; a centrifugation supernatant thereof; and a fraction obtained by partially purifying the supernatant with ammonium sulfate or the like.

The organic raw material to be used in the production method according to the present invention is not particularly restricted as long as it is a carbon source which can be assimilated by the microorganism of the present invention to produce succinic acid. As the organic raw material, usually, a fermentable sugar, for example, a carbohydrate such as galactose, lactose, glucose, fructose, glycerol, sucrose, saccharose, starch or cellulose or a polyalcohol such as glycerin, mannitol, xylitol or ribitol is used. Thereamong, glucose, sucrose or fructose is preferably used, and glucose or sucrose is particularly preferably used.

Further, a saccharified starch solution, molasses or the like, which contains the above-described fermentable sugar, may also be used, and specifically, a sugar solution collected from a plant such as sugarcane, sugar beet or sugar maple is preferred.

These sugars may be used individually or in combination. The concentration at which the above-described sugar is used is not particularly restricted; however, it is advantageous to increase the concentration as much as possible within the range which does not inhibit the production of succinic acid. The concentration of the above-described sugar is, with respect to the reaction solution, usually not lower than 5% (W/V), preferably not lower than 10% (W/V), and on another front, usually not higher than 30% (W/V), preferably not higher than 20% (W/V). Further, the above-described sugar may also be further added in response to a decrease thereof associated with the progression of the reaction.

The reaction solution containing the above-described organic raw material is not particularly restricted and it may be, for example, a medium for culturing a microorganism or a buffer solution such as phosphate buffer. The reaction solution is preferably an aqueous solution containing a nitrogen source, an inorganic salt and the like. Here, the nitrogen source is not particularly restricted as long as it can be assimilated by the microorganism of the present invention to produce succinic acid, and specific examples of such nitrogen source include a variety of organic and inorganic nitrogen compounds such as ammonium salts, nitrates, urea, soybean hydrolysates, casein digests, peptone, yeast extracts, meat extracts and corn steep liquors. As the inorganic salt, a variety of phosphates, sulfates and metal salts of magnesium, potassium, manganese, iron, zinc and the like may be used. Further, a growth-promoting factor(s) such as vitamins (e.g., biotin, pantothenic acid, inositol and nicotinic acid), nucleotides and amino acids may be added as required. Moreover, in order to suppress foam formation during reaction, it is desired to add an appropriate amount of a commercially available antifoaming agent to the reaction solution.

The reaction solution also contains a carbonate ion, bicarbonate ion or carbon dioxide gas in addition to the above-described organic raw material, nitrogen source and inorganic salt. The carbonate ion or the bicarbonate ion is supplied from magnesium carbonate, sodium carbonate, sodium bicarbonate, potassium carbonate, potassium bicarbonate or the like, which can also be used as a neutralizing agent; however, as required, the ion may also be supplied from carbonic acid or bicarbonic acid, or a salt thereof, or carbon dioxide gas. Specific examples of the salt of carbonic acid or bicarbonic acid include magnesium carbonate, ammonium carbonate, sodium carbonate, potassium carbonate, ammonium bicarbonate, sodium bicarbonate and potassium bicarbonate. Further, the carbonate ion or bicarbonate ion is added at a concentration of usually not lower than 1 mM, preferably not lower than 2 mM, more preferably not lower than 3 mM, and on another front, usually not higher than 500 mM, preferably not higher than 300 mM, more preferably not higher than 200 mM. In cases where carbon dioxide gas is added, it is contained in an amount of usually not less than 50 mg, preferably not less than 100 mg, more preferably not less than 150 mg, and on another front, usually not more than 25 g, preferably not more than 15 g, more preferably not more than 10 g, per 1 L of the solution.

The pH of the reaction solution can be adjusted by adding thereto, for example, sodium carbonate, sodium bicarbonate, potassium carbonate, potassium bicarbonate, magnesium carbonate, sodium hydroxide, calcium hydroxide, magnesium hydroxide or ammonia. The pH of the reaction is usually not lower than 5, preferably not lower than 5.5, more preferably not lower than 6, and on another front, not higher than 10, preferably not higher than 9.5, more preferably not higher than 9.0. Thus, during the reaction as well, the pH of the reaction solution is adjusted as required within the above-described range by adding thereto an alkaline substance, carbonate, urea or the like.

The optimum growth temperature of the microorganism to be used in the present reaction is not particularly restricted as long as it is a temperature at which the microorganism grows optimally; however, it is usually not lower than 25° C. but usually not higher than 35° C., preferably not higher than 32° C., particularly preferably not higher than 30° C. The term “optimum growth temperature” refers to a temperature at which the fastest growth rate is attained under the conditions used for the production of succinic acid.

Further, as a method of preparing bacterial cells more suitable for the production of succinic acid, the method described in JP 2008-259451A, in which culturing is performed by alternately repeating depletion and replenishment of a carbon source at short intervals, can also be employed.

The amount of the microorganism to be used in the reaction is not particularly restricted; however, in terms of the wet cell weight, the microorganism is used in an amount of usually not less than 1 g/L, preferably not less than 10 g/L, more preferably not less than 20 g/L, and on another front, usually not more than 700 g/L, preferably not more than 500 g/L, more preferably not more than 400 g/L. The reaction time is not particularly restricted; however, it is usually not short than 1 hour, preferably not shorter than 3 hours, and usually not longer than 168 hours, preferably not longer than 72 hours.

During the seed culturing of a microorganism, it is required that oxygen be supplied by aeration and stirring. On the other hand, although the reaction for producing an organic acid such as succinic acid may be carried out with aeration and stirring, it may also be carried out under an anaerobic atmosphere where aeration is not performed and oxygen is thus not supplied. Here, the condition “under an anaerobic atmosphere” can be attained by, for example, a method in which the reaction is carried out in a closed container with no aeration, a method in which the reaction is carried out with supply of an inert gas such as nitrogen gas or a method in which the reaction is carried out while aerating the system with a carbon dioxide-containing inert gas.

By such a microbial reaction as described in the above, an organic acid such as succinic acid, fumaric acid, malic acid or pyruvic acid is produced and accumulated in the reaction solution.

The amount of generated protocatechuic acid is, with respect to the amount of succinic acid produced in the culture medium after the reaction performed by allowing the microorganism of the present invention or a treated cell thereof to act on an organic raw material, usually not more than 500 ppm, preferably not more than 300 ppm, more preferably not more than 150 ppm, still more preferably not more than 75 ppm, particularly preferably not more than 50 ppm. There is no particular restriction with regard to the lower limit.

Further, the amount of generated uvitonic acid is, with respect to the amount of succinic acid produced in the culture medium after the reaction performed by allowing the microorganism of the present invention or a treated cell thereof to act on an organic raw material, usually not more than 500 ppm, preferably not more than 300 ppm, more preferably not more than 150 ppm, still more preferably not more than 75 ppm, particularly preferably not more than 50 ppm. There is no particular restriction with regard to the lower limit.

It is noted here that, also in cases where an organic acid other than succinic acid is produced, the concentration of protocatechuic acid and that of uvitonic acid are each, with respect to the organic acid of interest in the culture medium after the reaction, usually not more than 500 ppm, preferably not more than 300 ppm, more preferably not more than 150 ppm, still more preferably not more than 75 ppm, particularly preferably not more than 50 ppm.

The organic acid accumulated in the reaction solution (culture medium) can be recovered therefrom in accordance with a conventional method. The method of recovering from an organic acid from the reaction solution is not particularly restricted as long as a composition containing the desired organic acid can be obtained. By removing the microorganism, water and/or impurities from the reaction solution, an organic acid can be recovered.

The method of removing the microorganism, water and/or impurities is not particularly restricted and the removal can be achieved by a known method such as concentration, extraction, crystallization, an activated carbon treatment, a hydrogenation treatment or an ion-exchange column treatment or by an arbitrary combination of these known methods.

In the method of producing an organic acid according to the present invention, since the production of an aromatic carboxylic acid which is conventionally difficult to be removed by a crystallization treatment is reduced, it is preferred that the process of recovering an organic acid includes a crystallization treatment.

One example of such method of recovering an organic acid which includes crystallization is a method in which a microorganism is removed from a reaction solution and then, after concentrating the resulting reaction solution and extracting an organic acid as required, the resultant is subjected to crystallization, solid-liquid separation and drying. After the solid-liquid separation, for example, an activated carbon treatment, a hydrogenation treatment and/or an ion-exchange column treatment may also be performed.

A method of obtaining an organic acid, succinic acid, will now be described. However, the method of obtaining succinic acid is not restricted to the following description.

<Concentration>

In the present invention, a fermentation liquid obtained after the microbial reaction may also be concentrated as appropriate in consideration of the operability and efficiency in the subsequent purification step. The concentration method is not particularly restricted and examples thereof include a method in which an inert gas is allowed to circulate; a method in which water is distilled away by heating; a method in which water is distilled away under reduced pressure; and a combination of these methods. Further, the concentration operation may be performed in either a batch system or a continuous system.

<Removal of Microorganism>

In cases where a fermentation liquid is used in the method of the present invention, it is preferred that the fermentation liquid be one obtained after the removal of microorganism. The method of removing a microorganism is not particularly restricted and, for example, sedimentation separation, centrifugation, filtration separation and a method in which these techniques are combined can be employed. Industrially, the removal of microorganism is carried out by a method such as centrifugation or a membrane-filtration separation. As for the centrifugation, for example, centrifugal sedimentation or centrifugal filtration can be used. In the centrifugation, the operating conditions thereof are not particularly restricted; however, the separation is usually performed at a centrifugal force of 100 G to 100,000 G. Further, the operation may be performed in either a batch system or a continuous system.

Further, in the membrane-filtration separation, for example, microfiltration and/or ultrafiltration can be employed. The material of the membrane is not particularly restricted and, for example, an organic film of polyolefin, polysulfin, polyacrylonitrile, polyvinylidene fluoride or the like, or a membrane made of an inorganic material such as ceramic can be used. Further, the operation method may either be a dead-end type or a cross-flow type. In the membrane-filtration separation, since a microorganism often causes clogging of the membrane, for example, a method in which membrane filtration is performed after roughly removing the microorganism by centrifugation or the like may be employed as well.

In the production method according to the present invention, in cases where a neutralizing agent is used in the microbial reaction as described in the above, a salt of succinic acid is obtained, which is then converted into the desired succinic acid. This conversion into succinic acid may also be performed by a reactive crystallization method which utilizes a weakly acidic organic acid having an acid dissociation constant (pKa) higher than that of the desired succinic acid. Examples of such organic acid include acetic acid.

Further, alternatively, an inorganic acid may be used to convert the salt of succinic acid obtained in the above-described manner into succinic acid. Examples of the inorganic acid to be used in this method include sulfuric acid, hydrochloric acid, carbonic acid, phosphoric acid and nitric acid. More specifically, in the case of succinic acid fermentation, when fermentation is carried out while neutralizing the produced succinic acid with ammonia or magnesium hydroxide, ammonium succinate or magnesium succinate is produced in the resulting fermentation liquid. By treating such a fermentation liquid containing ammonium succinate or magnesium succinate with sulfuric acid or the like, a succinic acid-containing aqueous solution can be obtained.

In the present invention, the term “succinic acid-containing solution” or “succinic acid-containing aqueous solution” refers to a solution or an aqueous solution which mainly contains succinic acid derived from a biomass resource. Accordingly, a solution or an aqueous solution which mainly contains the above-described salt of succinic acid, such as ammonium succinate or magnesium succinate, is indicated as “succinate-containing solution” or “succinate-containing aqueous solution”. The term “mainly contain” used herein refers to a condition in which the solution or the aqueous solution contains the subject component in an amount of usually not less than 50% by weight, preferably not less than 60% by weight, more preferably not less than 70% by weight, particularly preferably not less than 90% by weight, with respect to the total weight of all components except the solvent.

<Extraction>

In the present invention, from an aqueous solution which contains succinic acid obtained by conversion with the above-described inorganic acid, succinic acid may be extracted by using, but not particularly limited to, an organic solvent.

The organic solvent to be used in this method is usually an organic solvent which has an inorganic value/organic value ratio (I/O value) of 0.2 to 2.3 and a boiling point of not lower than 40° C. at normal pressure, more preferably an organic solvent which has an I/O value of 0.3 to 2.0 and a boiling point of not lower than 40° C. at normal pressure, still more preferably an organic solvent which has an I/O value of 0.3 to 2.0 and a boiling point of not lower than 60° C. at normal pressure. By using such an organic solvent, succinic acid can be selectively extracted and efficiently separated from sugars and amino acids. Further, by using an organic solvent having a boiling point of not lower than 40° C. at normal pressure, it becomes possible to avoid the risk of the solvent being vaporized and ignited and a problem of a decrease in the efficiency of succinic acid extraction due to vaporization of the solvent as well as a problem of difficulty to recycle the solvent.

The inorganic value and the organic value are proposed by Organic Conceptual Diagram (“Systematic Organic Qualitative Analysis”, Fujita A., Kazamashobo Co., Ltd. (1974)). The ratio of the inorganic value and the organic value is determined by calculating the respective values based on the numerical values predetermined for the functional groups constituting the organic compound of interest.

Examples of the organic solvent which has an I/O value of 0.2 to 2.3 and a boiling point of not lower than 40° C. at normal pressure include ketone-based solvents such as methyl ethyl ketone, methyl isobutyl ketone and acetone; ether-based solvents such as tetrahydrofuran and dioxane; ester-based solvents such as ethyl acetate; nitrile-based solvents such as acetonitrile; and alcohols having a carbon chain of 3 or more carbon atoms, such as propanol, butanol and octanol.

The I/O value and boiling point of each solvent are shown below.

I O I/O Boiling point Tetrahydrofuran 30 80 0.375 66.0 Methyl ethyl ketone 65 60 1.083 79.6 Methyl isobutyl ketone 65 120 0.542 94.2 Acetone 65 40 1.625 56.1 Acetonitrile 70 40 1.750 81.1 Ethyl acetate 85 80 1.063 77.2 Propanol 100 60 1.667 97.2 Isobutanol 100 70 1.429 108.0 Octanol 100 160 0.625 179.8 Dioxane 40 80 0.500 101.3

In the extraction step, the organic solvent is added in a volume of, with respect to 1 volume of the succinic acid-containing aqueous solution, usually not less than 0.5, preferably not less than 1 and usually not more than 5, preferably not more than 3.

The temperature of the extraction step may be any temperature as long as it is a temperature at which succinic acid can be extracted; however, it is usually not lower than 10° C., preferably not lower than 20° C., while normally not higher than 90° C., preferably not higher than 85° C.

By the extraction step, succinic acid is recovered in the organic solvent and impurities such as sugars, elemental nitrogen originated from fermentation, ammonia originated from the fermentative bacterium, sulfur-containing impurities and metal cations are separated to some extent. Here, in order to extract succinic acid more efficiently, the extraction treatment with an organic solvent may be repeated a plurality of time, or countercurrent extraction may be performed.

<Removal of Impurities>

It is important that, in addition to the elemental nitrogen contained in the biomass resource, the amount of many impurities such as elemental nitrogen and ammonia originated from the fermentative bacterium, sulfur-containing impurities and metal cations be reduced from the succinic acid-containing fermentation liquid by purification. Further, it is also important to reduce the amount of impurities showing absorption in the ultraviolet region of 250 to 300 nm, particularly the amount of impurities containing an aromatic carboxylic acid, to a level where an average absorbance of 0.05 or lower is attained (see JP 2010-100617A).

In order to reduce the impurities contained in succinic acid that show absorbance in the ultraviolet region of 250 to 300 nm, particularly aromatic dicarboxylic acids, to a level where the average absorbance becomes 0.05 or lower, it is usually required to subject the succinic acid produced in the above-described manner to a combination of purification treatments such as a crystallization treatment, an activated carbon treatment, a hydrogenation treatment and a drying treatment. However, since the succinic acid-containing solution obtained by the fermentation method (organic acid production method) according to the present invention contains a markedly small amount of the above-described impurities as compared to a solution obtained by a conventional fermentation method (organic acid production method), the purification step of a crystallization treatment, an activated carbon treatment and the like can be reduced and the conditions thereof can be relaxed, so that the cost of producing an organic acid such as succinic acid can be reduced and the yield thereof can be improved, which are preferred.

<Crystallization>

In the present invent, succinic acid may also be recovered by crystallization from the succinic acid-containing solution obtained by the reaction. By performing a crystallization operation, the amount of aromatic carboxylic acids such as protocatechuic acid can be further reduced. In addition, in cases where crystallization is performed, as compared to a case where a conventional microorganism is employed, the number of crystallization operations can be reduced, which is useful.

In the present invention, the term “succinic acid crystallization” refers to an operation in which crystals of succinic acid are formed from a succinic acid-containing solution by changing the solubility of succinic acid with an application of a modification of some sort to the succinic acid-containing solution. For the succinic acid crystallization, any method may be employed as long as it is an operation which allows crystals of succinic acid to be formed from a succinic acid-containing fluid. More specifically, examples of such method include a cooling crystallization method in which succinic acid is precipitated by changing the temperature of a succinic acid-containing solution to utilize the temperature dependency of the solubility of succinic acid; a concentration-crystallization method in which succinic acid is precipitated out by evaporating a solvent from a solution by heating, pressure reduction or the like to thereby increase the concentration of succinic acid in the solution; a poor solvent crystallization method in which succinic acid is precipitated out by adding a third component (poor solvent), which reduces the solubility of succinic acid, to a succinic acid-containing solution; and a combination of these methods.

Further, in cases where the succinic acid-containing solution also contains a salt of succinic acid, crystals of succinic acid can be formed by adding a strong acid such as sulfuric acid or hydrochloric acid to the succinic acid-containing solution so as to convert the salt of succinic acid into succinic acid of non-dissociated form and then performing the above-described methods, such as cooling, concentration and addition of a poor solvent, in combination.

As for the cooling crystallization, examples of its cooling method include a method in which a succinic acid-containing solution is cooled by allowing it to circulate through an external heat exchanger or the like; a method in which a tube (inner coil) through which a coolant passes through is put into a succinic acid-containing solution; and a method in which the internal pressure of an apparatus is reduced to allow a solvent contained in a solution to be vaporized and cool the solution by means of the vaporization heat of the solvent. Thereamong, the method in which the internal pressure of an apparatus is reduced to allow a solvent contained in a solution to be vaporized and cool the solution by means of the vaporization heat of the solvent is preferred because not only inhibition of heat transfer, which is caused by succinic acid precipitating at the heat exchange interface, can be prevented, but also succinic acid can be concentrated in the solution. This method is preferred also from the standpoint of crystallization yield.

The concentration of succinic acid contained in the succinic acid-containing solution to be supplied to a crystallization bath is preferably 10% by weight to 45% by weight, more preferably 15% by weight to 40% by weight, particularly preferably 20% by weight to 35% by weight.

As a crystallization solvent, for example, water; an organic acid such as acetic acid or propionic acid; an ester such as ethyl acetate; an alcohol such as methanol, ethanol, propanol, isopropanol, butanol, 2-ethyl-1-hexanol or isobutanol; an ether such as diethyl ether, di-n-butyl ether, diisopropyl ether, di-n-butyl ether, tetrahydrofuran or dioxane; a ketone such as acetone, methyl ethyl ketone or diethyl ketone; a nitrile such as acetonitrile; or a mixture of these solvents can be employed. Thereamong, water is most preferred. As water, for example, deionized water, distilled water, river water, well water or tap water is usually used.

The temperature of a succinic acid-containing fluid in the crystallization bath at the time of crystallization (hereinafter, may be referred to as “the crystallization temperature”) is set to be a temperature at which succinic acid is crystallized from the succinic acid-containing fluid and it is usually 5° C. to 60° C., preferably 10° C. to 50° C. When the crystallization temperature is lower than 5° C., although succinic acid can be obtained in a high yield, an extremely large equipment is required for cooling. In addition, in a method where cooling is performed by circulating a coolant through a jacket or an inner coil, the difference in the temperature between succinic acid slurry and the coolant becomes excessively large at the heat-transfer surface to cause severe scaling, which is not desired. Thus, in the method where cooling is performed by circulating a coolant through a jacket or an inner coil, from the standpoint of preventing scaling, it is desired that the difference in the temperature between the succinic acid slurry and the coolant at the heat-transfer surface be set to be usually not larger than 20° C., preferably not larger than 10° C.

Further, the internal pressure of the crystallization bath to be used in the method in which crystallization is performed under reduced pressure is determined in accordance with the desired crystallization temperature, and it is usually 0.5 kPa to 20 kPa, preferably 1 kPa to 15 kPa, particularly preferably 1.5 kPa to 10 kPa. When the pressure is low, the temperature inside the crystallization bath can be further lowered and the crystallization efficiency can thus be improved; however, depending on the concentration of the succinic acid-containing fluid to be supplied, the slurry concentration in the crystallization bath may become excessively high, so that the handling thereof and/or pressure control may become difficult. Furthermore, the equipment to be used for pressure reduction is limited and the equipment cost is thus increased in general, which is not economically preferred. For example, in cases where steam ejectors are used for pressure reduction, an increase in the degree of pressure reduction leads to an increase in the equipment cost due to, for example, the necessity for increasing the number of the steam ejectors. On the other hand, when the pressure is high, the temperature inside the crystallization bath becomes high, so that the slurry concentration in the crystallization bath becomes excessively low to impair the crystallization efficiency. A vacuum-generating device can be selected from known means in accordance with the desired pressure as well as the presence or absence of a solvent to be evaporated with water, the type of the solvent and the like. Examples of the known means include those which are described in Design and Operation Series No. 3, revised, Crystallization (Sekkei-Sosa Series No. 3, kaitei, Shoseki; Kagaku Kogaku Sha, p. 292-293), such as water, steam ejectors and oil-sealed rotary vacuum pumps.

The crystallization operation may be performed in a batch system where, after loading the total amount of the succinic acid-containing fluid to be crystallized into the crystallization bath, the fluid is subjected to crystallization and then the total amount of the resulting fluid is recovered. Alternatively, the crystallization operation may be performed in a continuous system where, in order to prevent the crystallization bath from being emptied during the crystallization operation, the succinic acid-containing fluid is supplied and removed as appropriate while performing the crystallization operation.

In cases where crystallization is performed in a continuous system, in order to prevent the crystallization bath from being emptied, the supply of the succinic acid-containing fluid to the crystallization bath is carried out by, for example, a method in which the fluid is continuously or intermittently supplied with pressure by utilizing a liquid feed pump or a pressure difference. The succinic acid solution is usually supplied at such a rate at which the average residence time thereof in the crystallization bath is 0.5 hour to 10 hours. When the residence time in the crystallization bath is short, the supersaturation degree of succinic acid in the bath is increased, so that microcrystals are formed in a large amount. In addition, since the slurry is removed from the crystallization bath while maintaining a degree of supersaturation, there may arise problems of scaling and the like in the subsequent steps. Meanwhile, an excessively long residence time is also inefficient since it requires an unnecessarily large crystallization bath.

In cases where crystallization is performed in a continuous system, usually, the resulting succinic acid is recovered from the crystallization bath in the form of a slurry along with the succinic acid-containing fluid. In this case, the recovery is carried out by, for example, a method in which a slurry is, by means of pressurized transfer or the like which utilizes a pressure difference, continuously or intermittently recovered into a receiver tank having a pressure lower than that of the slurry pump or crystallization bath, while appropriately comparing the recovered amount and the supplied amount of the succinic acid-containing fluid so that the crystallization bath does not become empty.

In order to supply and recover the succinic acid-containing fluid to and from the crystallization bath in such a manner that the crystallization bath does not become empty, for example, a method in which the amount of supply and that of recovery are controlled to be the same or a method in which a fluid level sensor or the like is used to repeat an operation of supplying the fluid when the fluid level in the crystallization bath has declined to a certain level and an operation of removing the fluid when the fluid level has risen to a certain level can be employed.

In the crystallization operation, in order to control the particle size distribution of the resulting succinic acid crystals, it is desired that nucleation and crystal growth of succinic acid be controlled. The nucleation and crystal growth of succinic acid is usually controlled by adjusting the supersaturation degree of succinic acid in the bath and, for this purpose, a method in which the crystallization time is controlled is usually employed. The crystallization time is usually 0.5 hour to 10 hours, preferably 1 hour to 5 hours. For example, in cases where cooling crystallization operation is performed in a batch system, it is desired that the succinic acid-containing fluid be cooled to a prescribed temperature over a period of 0.5 hour to 5 hours and then aged for a period of 0.1 hour to 5 hours. In this process, the rate at which the succinic acid-containing fluid is cooled is usually 0.05° C./min to 2° C./min, preferably 0.1° C./min to 1.5° C./min, particularly preferably 0.2° C./min to 1° C./min. Further, in the cases where cooling crystallization operation is performed in a continuous system, it is desired that the average residence time of the succinic acid-containing fluid be 0.5 hour to 10 hours, preferably 1 hour to 5 hours. When the crystallization time or the average residence time is short, the supersaturation degree of succinic acid in the bath is increased and the nucleation rate becomes high, so that microcrystals are formed in a large amount. In addition, since the slurry is removed from the crystallization bath while maintaining a degree of supersaturation, there may arise problems of scaling and the like in the subsequent steps. Meanwhile, an excessively long crystallization time is also inefficient since it requires an unnecessarily large crystallization bath.

(Crystallization Bath)

The constitution of the crystallization bath is not particularly restricted as long as it is a vessel equipped with a stirring device. As the crystallization bath, a vessel having a conventionally known stirring device may be employed; however, a cylindrical vessel having a bottom is preferably employed. Further, in order to attain efficient shearing of the slurry, it is preferred that baffle plates be arranged inside the bath. Moreover, in order to control the flow inside the crystallization bath, a vessel having a cylindrical guide such as a guide called “draft tube” can also be employed.

The shape of the vessel is not particularly restricted; however, in order to make the slurry more uniform in the apparatus and to attain more efficient shearing of the slurry, the vessel has a ratio between the diameter and the height (L/D) of usually 0.5 to 3, preferably 0.7 to 2.5, particularly preferably 1 to 2.

(Stirring Device)

As a stirring device, one which is equipped with a stirring blades is employed. The stirring blade is not required to be a special blade and any known stirring blade can be used. The stirring blade is selected from, for example, shearing-type blades such as paddle blades and turbine blades; and discharge-type blades such as sweep-back blades, Pfaudler impellers, Maxblend Blade (registered trademark; Sumitomo Heavy Industries, Ltd.) and Fullzone Blade (registered trademark; Shinko Pantec Co., Ltd.).

The size of the stirring blade is also not particularly restricted, and another stirring device which circulates the fluid may also be used in combination of the stirring device equipped with a stirring blade.

As such stirring device, for example, a device which allows the succinic acid-containing solution transferred from the crystallization bath to be circulated back to the crystallization bath by means of a fluid transfer pump such as a centrifugal pump can be employed.

The stirring of the crystallization bath is not particularly restricted as long as the crystals of succinic acid are kept flowing without settling in the crystallization bath. From the standpoints that the purity of the resulting succinic acid can be improved and that succinic acid crystals having a more uniform particle size can be obtained, crystallization is performed under such stirring conditions where the power required for stirring a unit volume of the succinic acid-containing solution (hereinafter, may be abbreviated as “Pv”) is 0.2 kW/m³ to 5 kW/m³, preferably 0.4 kW/m³ to 3 kW/m³.

(Solid-Liquid Separation)

After the crystallization, the resulting succinic acid slurry can be subjected to a solid-liquid separation treatment in accordance with a known method to separate succinic acid crystals from the mother liquor. The separation method is not particularly restricted and examples thereof include filtration separation and sedimentation separation. Further, the separation operation may be performed either batchwise or continuously. Examples of an efficient solid-liquid separator include continuous-type centrifugal filtration apparatuses and centrifugal settlers such as decanters. In addition, depending on the desired purity of succinic acid, a wet cake recovered by the solid-liquid separation may be rinsed with cold water or the like.

(Drying)

The succinic acid recovered by crystallization can be dried by a conventional method depending on the application thereof. Generally, the succinic acid is dried to a water content of usually not less than 0.1% by weight, preferably not less than 0.2% by weight, and on another front, usually not higher than 2% by weight, preferably not higher than 1%. The drying method is not particularly restricted and, for example, a convection heating-type dryer such as a band dryer or a fluidized-bed dryer, or a conductive heat transfer-type dryer such as a drum dryer can be employed. A fluidized-bed dryer is particularly preferred since it is capable of performing a continuous treatment in a large quantity and the breakage of crystals in the process of drying treatment is limited. Further, when a fluidized-bed dryer is used, from the standpoint of preventing the succinic acid from causing dust explosion, it is preferred that the drying be performed under nitrogen supply and that the atmosphere be controlled to have an oxygen concentration of not higher than 12%. Moreover, since succinic anhydride may be generated as a result of intramolecular dehydration, the succinic acid is dried so that the temperature thereof during the drying process is maintained at preferably not higher than 100° C., more preferably not higher than 90° C., still more preferably not higher than 80° C.

Specific examples of a crystallization apparatus include the one shown in FIG. 4 which comprises an aqueous succinic acid solution feed tank; a crystallization bath having two rows of four baffle plates and four inclined paddle blades (stirring blades); a slurry recovery tank and the like.

<Activated Carbon Treatment>

In cases where an activated carbon treatment is performed, as the activated carbon to be used, any known activated carbon such as a coal-based activated carbon, a wood-based activated carbon, a coconut shell-based activated carbon or a resin-based activated carbon can be employed. In addition, activated carbons that are obtained by activating a variety of these material activated carbons, such as coal-based, wood-based, coconut shell-based and resin-based activated carbons, in accordance with a method such as a gas activation method, a steam activation method or a chemical activation method using zinc chloride, phosphoric acid or the like, can also be used.

Specific examples of such activated carbon include Calgon CPG, Calgon CAL, Calgon SGL, Diasorb W, Diahope MS10, Diahope M010, Diahope MS16, Diahope 6MD, Diahope 6MW, Diahope 8ED, Diahope ZGN4 and Centur, all of which are manufactured by Calgon-Mitsubishi Chemical Corporation; GAC, GAC PLUS, GCN PLUS, C GRAN, RO, ROX, DARCO, CN, SX, SXPLUS, SA, SX, PK and W, all of which are manufactured by Norit Japan Co., Ltd.; GW, GWH, GLC, 4GC, KW, PW and PK, all of which are manufactured by Kuraray Chemical Co., Ltd.; HC-30S, GL-30S, 4G-3S, PA and PC, all of which are manufactured by Tsurumicoal Co., Ltd.; P, W, CW, SG, SGP, S, GB, CA and K, all of which are manufactured by Futamura Chemical Co., Ltd.; Shirasagi KL, Shirasagi W2C, Shirasagi WH2C, Shirasagi W5C, Shirasagi WH5C, Shirasagi WH5X, Shirasagi XS7100H-3, Carboraffin, Shirasagi A, Shirasagi C and Shirasagi M, all of which are manufactured by Japan EnviroChemicals Ltd.; and Hokuetsu CL-K, Hokuetsu HS and Hokuetsu KS, all of which are manufactured by Ajinomoto Fine-Techno Co., Inc.

Among these activated carbons, coconut shell-based activated carbons and wood-based activated carbons are preferred since they are capable of efficiently removing impurities showing absorption in the ultraviolet region of 250 to 300 nm that are contained in succinic acid. Meanwhile, from the standpoint of efficiently removing a color component of succinic acid, activated carbons that are obtained by a method such as a gas activation method, a steam activation method or a chemical activation method using zinc chloride, phosphoric acid or the like are preferred. Thereamong, activated carbons that are obtained by a steam activation method or a chemical activation method using zinc chloride, phosphoric acid or the like are more preferred and activated carbons that are activated with a chemical agent such as zinc chloride or phosphoric acid are particularly preferred. The shape of the activated carbon to be used may take any of a powder form, a crushed form, a molded form and a fibrous form. In cases where the activated carbon is loaded into a column, from the standpoint of controlling the column pressure, the activated carbon is preferably in the form of particles or granules.

As a method of the activated carbon treatment, either a method in which a succinic acid-containing solution is mixed with an activated carbon in a batchwise manner and the resulting mixture is then separated by filtration or a method in which the solution is passed through a packed bed of an activated carbon can be employed. In cases where a batch system is used, the treatment time is usually not shorter than 5 minutes, preferably not shorter than 10 minutes, and on another front, usually not longer than 5 hours, preferably not longer than 2 hours. In cases where a packed bed system is used, the treatment time is, in terms of SV (space velocity), usually 0.1 hr⁻¹ to 20 hr⁻¹. The treatment temperature is usually 20° C. to 90° C. As described in the above, the type of impurities to be removed is different depending on the type of the activated carbon; therefore, as a method of removing the impurities, for example, a method in which a plural types of activated carbons are used in combination or a method in which an activated carbon treatment is performed in combination with the above-described crystallization treatment, the below-described hydrogenation treatment and/or the below-described ion-exchange column treatment can be employed.

Further, in cases where water is used as a solvent, a succinic acid solution derived from fermentation may contain a component insoluble to water. Inclusion of such an insoluble component causes a reduction in the efficiency of removing the above-described impurities by an activated carbon and the subsequent purification step; therefore, it is preferred that such an insoluble component be removed in advance. Removal of the insoluble component is preferably carried out by a method in which, in-between the step of deriving succinic acid from a generated salt of succinic acid by a fermentation method and the step of performing an activated carbon treatment, the insoluble component is removed from a succinic acid solution originated from fermentation by subjecting the solution to a known membrane permeation treatment. Alternatively, a method in which the permeability of a membrane permeation treatment is improved by allowing the insoluble component to be adsorbed under the coexistence of powder-form activated carbon or a method in which an appropriate powder-form activated carbon is used to adsorb and remove the insoluble component simultaneously with the above-described impurities can also be suitably employed.

Further, in the present invention, in cases where removal of impurities is carried out by performing a crystallization treatment and/or an activated carbon treatment in combination with a hydrogenation treatment, for example, but not particularly limited to, a process in which the step of crystallization and/or activated carbon treatment is carried out prior to the below-described hydrogenation treatment step is suitably employed since such a process efficiently removes the impurities.

<Hydrogenation Treatment>

Succinic acid obtained by a microbial reaction usually contains an odor component. It is preferred that the amount of the odor component in the succinic acid be reduced.

As a method for removing an odor component, there are known, for example, a deodorization method which utilizes an adsorbent such as an activated carbon; a method in which an odor component is removed by washing with an organic solvent; a crystallization method; and an aeration method. For removal of an odor component, a hydrogenation treatment in the presence of a catalyst is particularly effective. Meanwhile, a succinic acid-containing solution derived from a biomass resource by fermentation or the like may contain a small amount of fumaric acid.

When a succinic acid-containing solution derived from a biomass resource by fermentation or the like is subjected to a hydrogenation treatment, not only the odor component contained in succinic acid can be easily removed, but also, in cases where the solution contains fumaric acid as described above, succinic acid is generated from fumaric acid and the yield of succinic acid can thus be improved at the same time; therefore, as a method for deodorizing succinic acid, such hydrogenation treatment method is an exceptional technique as compared to conventional methods. It is preferred that the purification process include the step of subjecting a succinic acid-containing solution derived from fermentation to a hydrogenation treatment in the presence of a catalyst.

The hydrogenation treatment may take either a batchwise reaction system or a continuous reaction system and can be performed in accordance with a conventionally known method. Specific examples of the hydrogenation treatment method include a method in which, after allowing a succinic acid-containing solution and a hydrogenation catalyst to coexist in a pressurized reactor and subjecting this mixture to a hydrogenation treatment with stirring by introducing a hydrogen gas thereto, the thus treated succinic acid-containing reaction solution is separated from the hydrogenation catalyst and recovered from the reactor; a method in which a hydrogenation treatment is performed using a fixed-bed multi-tubular reactor or a single-tubular reactor while circulating a succinic acid-containing solution and hydrogen gas from a lower section of the reactor and the thus treated succinic acid-containing reaction solution is then recovered; and a method in which a hydrogenation treatment is performed by introducing a hydrogen gas from a lower section of a reactor and circulating a succinic acid-containing solution from an upper section of the reactor and the thus treated succinic acid-containing reaction solution is then recovered.

As the hydrogenation catalyst, a known homogeneous or heterogeneous noble metal-containing hydrogenation catalyst can be employed. Specific examples of such hydrogenation catalyst include, but not particularly limited to, those hydrogenation catalysts containing a noble metal such as ruthenium, rhodium, palladium or platinum. Thereamong, hydrogenation catalysts containing palladium or platinum, particularly palladium, are preferred.

These hydrogenation catalysts may be used as-is in the form of a compound containing the above-described noble metal or may be used in a form in which a ligand such as organic phosphine is allowed to coexist; however, from the standpoint of the easiness of catalyst separation, a heterogeneous noble metal-containing catalyst is preferred.

Further, a hydrogenation treatment can be performed by using such a noble metal-containing compound in coexistence with a metal oxide such as silica, titania, zirconia or activated alumina, a complex metal oxide thereof or an activated carbon. This method is preferred because, not only an odor component contained in succinic acid derived from fermentation, but also color components and organic impurities can be simultaneously adsorbed and removed, so that efficient removal of impurities can be achieved. The same effects can be attained also by using a catalyst prepared by supporting the above-described noble metal on a carrier such as a metal oxide (e.g., silica, titania, zirconia or activated alumina), a complex metal oxide thereof or an activated carbon; therefore, a method in which such a supported catalyst is used can also be suitably employed. The amount of the noble metal to be supported is usually 0.1 to 10% by weight of the carrier. The carrier is not particularly restricted; however, it is preferably silica or an activated carbon, particularly preferably an activated carbon, since the amount of the metal eluting therefrom during the hydrogenation treatment is small.

Accordingly, in the present invention, the embodiment in which a hydrogenation treatment is performed with a hydrogenation catalyst prepared by supporting a noble metal on a carrier such as a metal oxide (e.g., silica, titania, zirconia or activated alumina), a complex metal oxide thereof or an activated carbon is included in the definition of an embodiment in which a hydrogenation treatment is performed with a hydrogenation catalyst in the presence of an adsorbent selected from the group consisting of metal oxides, silica and activated carbons.

As a solvent into which succinic acid derived from a biomass resource is incorporated at the time of the hydrogenation treatment, water; an organic acid such as acetic acid or propionic acid; an ester such as ethyl acetate; an alcohol such as methanol, ethanol, propanol, isopropanol, butanol, 2-ethyl-1-hexanol or isobutanol; an ether such as diethyl ether, di-n-butyl ether, diisopropyl ether, di-n-butyl ether, tetrahydrofuran or dioxane; a ketone such as acetone, methyl ethyl ketone or diethyl ketone; a nitrile such as acetonitrile; or a mixture of these solvents can be employed. Thereamong, water is most preferred. As water, for example, deionized water, distilled water, river water, well water or tap water is usually used. As required, a solution, which is obtained as a result of the step of crystallizing succinic acid from a succinic acid-containing reaction solution after hydrogenation reaction and the subsequent filtration, can also be repeatedly used. The solution may have any succinic acid concentration as long as it is not higher than the saturation solubility at the solution temperature.

The hydrogen gas to be used may be pure hydrogen; however, hydrogen diluted with an inert gas such as nitrogen, helium or argon can also be used. In consideration of the effect on the efficiency of the hydrogenation treatment, the concentration of carbon monoxide in the hydrogen gas is usually not higher than 10,000 ppm, preferably not higher than 2,000 ppm, more preferably not higher than 1,000 ppm.

As for the hydrogen pressure in the hydrogenation treatment, when it is excessively low, the reaction rate becomes slow, so that a long time is required to complete the reaction. Meanwhile, when the hydrogen pressure is excessively high, depending on the catalyst and reaction conditions, hydrides of succinic acid such as butanediol and tetrahydrofuran are generated as by-products. Therefore, the hydrogen pressure in the hydrogenation treatment is usually not lower than 0.1 MPa, and the upper limit thereof is usually not higher than 5 MPa, preferably not higher than 3 MPa, more preferably not higher than 1 MPa.

As for the temperature of the hydrogenation treatment, when it is excessively low, the reaction rate becomes slow, so that a long time is required to complete the reaction. Meanwhile, when the temperature is excessively high, hydrides of succinic acid are generated as by-products and the amount of by-products such as malic acid is increased when water is used as the solvent. Therefore, the temperature of the hydrogenation treatment is usually not lower than 30° C., preferably not lower than 50° C., and the upper limit thereof is usually not higher than 150° C., preferably not higher than 120° C.

<Ion-Exchange Column Treatment>

Further, in the present invention, in order to remove impurities contained in succinic acid, a purification operation such as an ion-exchange column treatment may also be performed in combination.

The term “ion-exchange column treatment” used herein refers to a process of removing an ion by treating the liquid to pass through a column loaded with an ion-exchange resin. The ion-exchange resin should be selected in accordance with the ions contained in the liquid to be treated and the required purity of succinic acid. For example, in order to remove an anion such as sulfate ion or chloride ion, an anion-exchange resin (OH-type) can be employed and, in order to remove a cation such as a metal ion or ammonium ion, a cation-exchange resin (H-type) can be employed. These ion-exchange resins may also be used in combination as required.

Ion-exchange resins are classified into strongly acidic cation-exchange resins, weakly acidic cation-exchange resins, strongly basic anion-exchange resins and weakly basic anion-exchange resins, based on the strength of the functional group as an acid or a base. Further, based on the form thereof, ion-exchange resins are also classified into gel-type and porous-type. In the present invention, the ion-exchange resin to be used is not particularly restricted. However, taking into consideration the ion exchange efficiency, it is preferred to use a strongly acidic cation-exchange resin having a higher strength as an acid and/or a strongly basic anion-exchange resin having a higher strength as a base. Moreover, since there is no particular reason that the ion-exchange resin has to be a porous-type, it is desired to use a more versatile and inexpensive gel-type ion-exchange resin. Specific examples of such cation-exchange resin include Diaion SK1B (H-type) and specific examples of such anion-exchange resin include Diaion SA10A.

The ion-exchange column treatment can be performed within the temperature range which is not lower than the temperature at which succinic acid is dissolved in the liquid to be treated but lower than the heat-resistant temperature of the ion-exchange resin. That is, in cases where a cation-exchange resin is used, the ion-exchange column treatment is usually performed at a temperature of 20 to 100° C., although this is variable depending on the concentration of succinic acid in the liquid to be treated. Meanwhile, since an anion-exchange resin has a lower heat resistance as compared to a cation-exchange resin, in cases where an anion-exchange resin is used, the ion-exchange column treatment is usually performed at a temperature of 10 to 80° C. From the standpoint of the treatment temperature, in cases where an anion-exchange column treatment is performed, it is desired that a step in which a column treatment can be performed at a low succinic acid concentration and a low temperature be adopted.

Further, the method of allowing a liquid to pass through a column for treatment is not particularly restricted. When the throughput rate is excessively high, the pressure loss before and after the column is increased and the ion exchange is not sufficiently performed, while when the throughput rate is needlessly slow, an unnecessarily large column is required. Therefore, the treatment is usually performed at a space velocity (SV) of 0.1 to 10 hr⁻¹ and a superficial velocity of 1 to 20 m/hr.

Usually, in a column treatment, the ion concentration is measured at the column outlet at all times or at regular intervals and, if ion leakage were detected at the column outlet, the ion-exchange resin is subjected to a regeneration treatment. Regeneration of the ion-exchange resin can be carried out in accordance with a conventional method by using an acid such as sulfuric acid or hydrochloric acid in the case of a cation-exchange resin or an alkali such as caustic soda in the case of an anion-exchange resin.

The organic acid such as succinic acid obtained by the production method of the present invention contains a small amount of the above-described impurities such as an aromatic carboxylic acid, and the organic acid has an average absorbance of preferably not higher than 0.05, more preferably not higher than 0.03, particularly preferably not higher than 0.01, in the ultraviolet region of 250 to 300 nm. When succinic acid having a high average absorbance is used as a starting material of a polyester, a markedly colored polymer is produced.

In the present invention, the term “absorbance” refers to a value which is obtained by measuring a 3.0%-by-weight aqueous succinic acid solution placed in a quartz cell of 1 cm in optical path length by using an ultraviolet-visible absorption spectrophotometer. The measurement of absorbance can be performed by using a commercially available ultraviolet-visible absorption spectrophotometer.

The term “absorbance (A)” used herein means an absorbance measured at an optical path length of 1 cm and it is calculated in accordance with the following definition. A=log 10(I ₀ /I)

(wherein, I₀ represents the intensity of incident light; and I represents the intensity of transmitted light.)

Further, the term “average absorbance in the ultraviolet region of 250 to 300 nm” means a value which is obtained by dividing the sum of absorbances measured at 1 nm intervals in the wavelength range of 250 to 300 nm by 51. Average absorbance=(Sum of absorbances measured at 1 nm intervals in the wavelength region of 250 to 300 nm)/51

The concentration of protocatechuic acid is, with respect to the succinic acid obtained by the production method of the present invention, preferably not higher than 80 ppm, more preferably not higher than 30 ppm, still more preferably not higher than 15 ppm, yet still more preferably not higher than 10 ppm, further still more preferably not higher than 5 ppm, particularly preferably not higher than 3 ppm. When the concentration of protocatechuic acid is high, the coloration of the resulting polymer is increased. Further, in order to control the concentration of protocatechuic acid at a low level, an excessive purification treatment is required; however, its polymer coloration-improving effect is limited and not efficient.

The concentration of uvitonic acid is, with respect to the succinic acid obtained by the production method of the present invention, preferably not higher than 300 ppm, more preferably not higher than 150 ppm, still more preferably not higher than 100 ppm, yet still more preferably not higher than 30 ppm, particularly preferably not higher than 10 ppm. When the concentration of uvitonic acid is high, the coloration of the resulting polymer is increased. Further, in order to control the concentration of protocatechuic acid at a low level, an excessive purification treatment is required; however, its polymer coloration-improving effect is limited and not efficient.

Here, also in cases where an organic acid other than succinic acid is produced, the concentration of protocatechuic acid is, with respect to the organic acid of interest obtained by the production method of the present invention, preferably not higher than 80 ppm, more preferably not higher than 30 ppm, still more preferably not higher than 15 ppm, yet still more preferably not higher than 10 ppm, further still more preferably not higher than 5 ppm, particularly preferably not higher than 3 ppm. Moreover, the concentration of uvitonic acid is, with respect to the organic acid of interest obtained by the production method of the present invention, preferably not higher than 300 ppm, more preferably not higher than 150 ppm, still more preferably not higher than 100 ppm, yet still more preferably not higher than 30 ppm, particularly preferably not higher than 10 ppm.

Further, it is usually preferred that the succinic acid produced in the present invention have a low absorbance in the visible light region and a low level of coloration. As for the yellowness (Y.I. value) of the succinic acid, the upper limit thereof is usually not higher than 50, preferably not higher than 30, more preferably not higher than 20, still more preferably not higher than 10, yet still more preferably not higher than 6, particularly preferably not higher than 4, while the lower limit thereof is, though not particularly restricted, usually not lower than −10, preferably not lower than −5, more preferably not lower than −1. When succinic acid showing a high Y.I. value is used as a starting material of a polymer, there is a drawback that a markedly colored polymer is produced. Meanwhile, succinic acid showing a low Y.I. value is a more preferred mode; however, from the economical standpoint, such succinic acid has disadvantages in that, for example, the production thereof requires a huge investment to be made in equipments and is considerably time-consuming. In the present invention, the Y.I. value is measured by the method according to JIS K7105.

The organic acid such as succinic acid obtained by the production method of the present invention may contain, as an impurity, elemental nitrogen which is originated from a biomass resource or generated by a fermentation treatment or a purification treatment including a step of performing neutralization with an acid. More specifically, the organic acid obtained by the production method of the present invention may contain elemental nitrogen originated from an amino acid, a protein, an ammonium salt, urea, a fermentative bacterium or the like.

The upper limit of the nitrogen atom content in the organic acid such as succinic acid obtained by the production method of the present invention is, in terms of the amount of atoms, usually not higher than 2,000 ppm, preferably not higher than 1,000 ppm, more preferably not higher than 100 ppm, most preferably not higher than 20 ppm. The lower limit of the nitrogen atom content is usually not less than 0.01 ppm, preferably not less than 0.05 ppm, and from the standpoint of economical efficiency of the purification step, more preferably not less than 0.1 ppm, still more preferably not less than 1 ppm.

The nitrogen atom content is measured by a known method such as an elemental analysis method or a method in which, after separating an amino acid or ammonia from a sample under a biological amino acid separation condition using an amino acid analyzer, the thus separated amino acid or ammonia is subjected to ninhydrin coloration and then detected.

In cases where succinic acid having a nitrogen atom content in the above-described range is used as a starting material of a polyester, the coloration of the resulting polyester is reduced, which is advantageous. In addition, the use of such succinic acid also has an effect of inhibiting a delay in the polymerization reaction of polyester.

Further, the organic acid such as succinic acid obtained by the production method of the present invention may also contain a sulfur atom generated by, for example, a purification treatment which includes a step of performing neutralization with an acid. Specific examples of impurities containing a sulfur atom include sulfuric acid, sulfates, sulfurous acid, organic sulfonic acids and organic sulfonates.

The sulfur atom content in the organic acid such as succinic acid obtained by the production method of the present invention is not particularly restricted; however, when it is excessively high, the use of the organic acid as a starting material of a polyester tends to cause, for example a delay in the polymerization reaction, partial gelation of the generated polymer and a reduction in the stability of the generated polymer. On the other hand, an excessively low sulfur atom content makes the purification step complicated. Therefore, the upper limit of the sulfur atom content in a dicarboxylic acid is, in terms of the amount of atoms, usually not higher than 100 ppm, preferably not higher than 20 ppm, more preferably not higher than 10 ppm, particularly preferably not higher than 5 ppm, most preferably not higher than 0.5 ppm. Meanwhile, the lower limit of the sulfur atom content is usually not less than 0.001 ppm, preferably not less than 0.01 ppm, more preferably not less than 0.05 ppm, particularly preferably not less than 0.1 ppm. Here, the sulfur atom content is measured by a known elemental analysis method.

The organic acid such as succinic acid obtained by the production method of the present invention may contain an alkali metal element. When the alkali metal content in an aliphatic dicarboxylic acid is excessively high, the use thereof as a starting material of a polymer not only reduces the thermal stability and hydrolysis resistance, but also causes a severe inhibition of polymerization during polymerization, so that a polymer of a high polymerization degree which has practically sufficient mechanical characteristics may not be obtained. Therefore, the alkali metal content is usually not higher than 50 ppm, preferably not higher than 30 ppm, more preferably not higher than 10 ppm, particularly preferably not higher than 5 ppm.

<Method of Producing Polymer>

Further, in the present invention, after producing an organic acid such as succinic acid in accordance with the above-described method, by performing a polymerization reaction using the thus obtained organic acid as a starting material, an organic acid-containing polymer can be produced. In recent years, with an increasing number of environment-friendly industrial products, polymers prepared from a material of plant origin have been drawing attention. Particularly, the succinic acid produced in the present invention can be processed into known polymers that are produced by using a dicarboxylic acid component, preferably an aliphatic dicarboxylic acid as a starting material, such as polyesters, polyamides and polyurethanes. Specific examples of succinic acid unit-containing polymers include polyesters that are obtained by polymerization between a diol such as butanediol or ethylene glycol and succinic acid; and polyamides that are obtained by polymerization between a diamine such as hexamethylenediamine and succinic acid.

As one example of the method of producing a polymer, a method of producing a polyester will now be described.

<Method of Producing Polyester>

In the present invention, as a method of producing a polyester, a conventionally known method can be employed. For example, a polyester can be produced by a commonly used melt-polymerization method in which an esterification reaction and/or a transesterification reaction is carried out between an aliphatic dicarboxylic acid component containing the above-described succinic acid and a diol component and the resultant is then subjected to a polycondensation reaction under reduced pressure or by a known solution-heating dehydration condensation method in which an organic solvent is used; however, from the standpoint of economical efficiency and simplicity of the production process, a method in which a polyester is produced by melt polymerization in the absence of solvent.

<Dicarboxylic Acid Component>

The dicarboxylic acid component is not particularly restricted as long as it contains the succinic acid obtained by the above-described method of producing an organic acid. The dicarboxylic acid component may contain an aliphatic and/or aromatic dicarboxylic acid derived from a fossil resource; however, it is preferred that the dicarboxylic acid component contain the succinic acid obtained by the above-described method of producing an organic acid.

<Diol Component>

The diol component is not particularly restricted; however, it is preferably an aliphatic diol.

The aliphatic diol is not particularly restricted as long as it is an aliphatic or alicyclic compound having two OH groups, and examples thereof include aliphatic diols in which the lower limit of the number of carbon atoms is not less than 2 and the upper limit is usually not more than 10, preferably not more than 6.

Specific examples of such aliphatic diol include ethylene glycol, 1,3-propylene glycol, neopentylglycol, 1,6-hexamethylene glycol, decamethylene glycol, 1,4-butanediol and 1,4-cyclohexanedimethanol. These aliphatic diols may be used individually, or two or more thereof may be used in combination as a mixture.

Thereamong, ethylene glycol, 1,4-butanediol, 1,3-propylene glycol and 1,4-cyclohexanedimethanol are preferred and ethylene glycol, 1,4-butanediol and a mixture thereof are more preferred. Further, an aliphatic diol containing 1,4-butanediol as a main component or 1,4-butanediol is particularly preferred. The term “main component” means that the amount of the component is, with respect to the total amount of diol units, usually not less than 50 mol %, preferably not less than 60 mol %, more preferably not less than 70 mol %, particularly preferably not less than 90 mol %.

Further, a polyether terminated with a hydroxy group at both ends may also be used in combination with the above-described aliphatic diol. In the polyether terminated with a hydroxy group at both ends, the lower limit of the number of carbon atoms is usually not less than 4, preferably not less than 10, and the upper limit is usually not more than 1,000, preferably not more than 200, more preferably not more than 100.

Specific examples of such polyether terminated with a hydroxy group at both ends include diethylene glycol, triethylene glycol, polyethylene glycol, polypropylene glycol, polytetramethylene glycol, poly-1,3-propanediol and poly-1,6-hexamethylene glycol. Further, for example, a copolymer polyester composed of polyethylene glycol and polypropylene glycol can also be used. The amount of the polyether terminated with a hydroxy group at both ends to be used is, in terms of the content in the resulting polyester, a calculated amount of usually not more than 90% by weight, preferably not more than 50% by weight, more preferably not more than 30% by weight.

<Other Copolymer Component>

In the production of a polyester according to the present invention, in addition to the above-described diol component and dicarboxylic acid component, a copolymer component may be added as well.

Specific examples of the copolymer component include at least one polyfunctional compound selected from the group consisting of bifunctional oxycarboxylic acids, unsaturated dicarboxylic acids, tri- or higher functional polyhydric alcohols for forming a cross-linked structure, tri- or higher functional polycarboxylic acids or anhydrides thereof and tri- or higher functional oxycarboxylic acids. When these copolymer components are added, an effect of considerably improving the polymerization rate in the polyester production is exerted. Among these copolymer components, an oxycarboxylic acid is suitably employed since it tends to allow a polyester having a high polymerization degree to be easily produced.

Specific examples of the bifunctional oxycarboxylic acids include lactic acid, glycolic acid, hydroxybutyric acid, hydroxycaproic acid, 2-hydroxy-3,3-dimethylbutyric acid, 2-hydroxy-3-methylbutyric acid and 2-hydroxyisocaproic acid, and these may also be in the form of an ester or lactone of an oxycarboxylic acid or a derivative of an oxycarboxylic acid polymer or the like. Further, these oxycarboxylic acids may be used individually, or two or more thereof may be used in combination as a mixture. In cases where these oxycarboxylic acids have optical isomers, they may also be any of a D-isomer, an L-isomer and a racemic body. Moreover, these oxycarboxylic acids may be in the form of a solid, a liquid or an aqueous solution. Thereamong, readily available lactic acid and glycolic acid are particularly preferred. As for the form thereof, a 30 to 95% aqueous solution is preferred since such an aqueous solution is readily available. In this case, the lower limit of the amount of the oxycarboxylic acid to be used is, with respect to the amount of the material monomer, usually not less than 0.02 mol %, preferably not less than 0.5 mol %, more preferably not less than 1.0 mol %, while the upper limit thereof is usually not more than 30 mol %, preferably not more than 20 mol %, more preferably not more than 10 mol %.

Examples of the unsaturated dicarboxylic acids include itaconic acid, aconitic acid, fumaric acid and maleic acid. These unsaturated dicarboxylic acids may be used individually, or two or more thereof may be used in combination as a mixture. Since an unsaturated dicarboxylic acid causes generation of a gel, the amount of the unsaturated dicarboxylic acid to be used is, with respect to the total amount of monomer units constituting the polyester, usually not more than 5 mol %, preferably not more than 0.5 mol %, more preferably not more than 0.05 mol %.

Specific examples of the tri- or higher functional polyhydric alcohols include glycerin, trimethylolpropane and pentaerythritol. These tri- or higher functional polyhydric alcohols may be used individually, or two or more thereof may be used in combination as a mixture.

Specific examples of the tri- or higher functional polycarboxylic acids or anhydrides thereof include propanetricarboxylic acids, pyromellitic acid anhydrides, benzophenonetetracarboxylic acid anhydrides and cyclopentatetracarboxylic acid anhydrides, and these may be used individually, or two or more thereof may be used in combination as a mixture.

Specific examples of the tri- or higher functional oxycarboxylic acids include malic acid, hydroxyglutaric acid, hydroxymethylglutaric acid, tartaric acid, citric acid, hydroxyisophthalic acid and hydroxyterephthalic acid. These tri- or higher functional oxycarboxylic acids may be used individually, or two or more thereof may be used in combination as a mixture. In particular, from the standpoint of availability, malic acid, tartaric acid and citric acid are preferred.

Since the above-described tri- or higher functional compounds cause generation of a gel, the amount thereof to be used is, with respect to the total amount of monomer units constituting the polyester, usually not more than 5 mol %, preferably not more than 0.5 mol %, more preferably not more than 0.2 mol %.

For the conditions of temperature, time, pressure and the like, conventionally known ranges can be adopted.

With regard to the temperature of the esterification reaction and/or the transesterification reaction performed between a succinic acid-containing aliphatic dicarboxylic acid component and a diol component, the lower limit is usually not lower than 150° C., preferably not lower than 180° C., and the upper limit is usually not higher than 260° C., preferably not higher than 250° C. As for the reaction atmosphere, these reactions are usually performed under an inert gas atmosphere such as nitrogen or argon. The reaction pressure is usually in normal pressure to 10 kPa, preferably normal pressure.

The reaction time is usually not shorter than 1 hour and the upper limit thereof is usually not longer than 10 hours, preferably not longer than 4 hours.

In the subsequent polycondensation reaction, when the pressure at the time of producing a polyester by polymerization is excessively high, the time required for the production is extended and, as a result, a reduction in the molecular weight and coloration of the resulting polyester are caused by thermal decomposition, so that it tends to become difficult to produce a polyester which exhibits practically sufficient characteristics. Meanwhile, from the standpoint of improving the polymerization rate, a method in which a polyester is produced by using an ultra-high vacuum polymerization equipment is a preferred embodiment; however, not only a huge investment needs to be made into equipments, but also the time required for a polyester to be produced by polymerization still tends to be long; therefore, there are concerns for a reduction in the molecular weight and coloration of the resulting polyester that are caused by thermal decomposition. Accordingly, the polycondensation reaction is performed at a vacuum degree of, as the lower limit, usually not lower than 0.01×10³ Pa, preferably not lower than 0.01×10³ Pa and, as the upper limit, usually not higher than 1.4×10³ Pa, preferably not higher than 0.4×10³ Pa.

As for the reaction temperature, when it is excessively low, the rate of polymerization reaction becomes extremely slow, so that not only the time required for the production of a polyester having a high polymerization degree is extended, but also a high-power stirring machine becomes necessary; therefore, the use of such a low reaction temperature is economically disadvantageous. Meanwhile, when the reaction temperature is excessively high, although the polymerization rate is improved, thermal decomposition of the polymer is also induced during the production, making it difficult to produce a polyester having a high polymerization degree. Accordingly, the lower limit of the reaction temperature is usually not lower than 150° C., preferably not lower than 180° C., while the upper limit thereof is usually not higher than 280° C., preferably not higher than 260° C.

As for the reaction time, when it is excessively short, the reaction proceeds insufficiently to yield a polyester having a low polymerization degree. The resulting polyester exhibits a low tensile elongation at break and has a large amount of terminal carboxyl group, which often causes considerable deterioration in the tensile elongation at break. Meanwhile, when the reaction time is excessively long, since the molecular weight of the resulting polyester is markedly reduced due to thermal decomposition, not only the tensile elongation at break may be impaired, but also the amount of terminal carboxyl group, which affects the durability of polymer, may be increased due to thermal decomposition. Accordingly, the lower limit of the reaction time is usually not shorter than 2 hours, while the upper limit thereof is usually not longer than 15 hours, preferably not longer than 8 hours, more preferably not longer than 6 hours.

In the present invention, with regard to the molar ratio of the diol component and the aliphatic dicarboxylic acid component required for obtaining a polyester having a desired polymerization degree, the preferred range thereof is variable depending on the purpose thereof and the types of the starting materials; however, the lower limit of the amount of the diol component is, per 1 mol of acid component, usually not less than 0.8 mol, preferably not less than 0.9 mol, while the upper limit thereof is usually not more than 3.0 mol, preferably not more than 2.7 mol, particularly preferably not more than 2.5 mol.

Further, in the present invention, it is preferred that the polycondensation reaction be carried out in the presence of a polymerization catalyst. The timing of adding the polymerization catalyst is not particularly restricted as long as it is before the polycondensation reaction. The polymerization catalyst may be added at the time of feeding the starting materials or at the start of pressure reduction.

Examples of the polymerization catalyst generally include those compounds other than hydrogen and carbon that contain a metal element belonging to the Groups 1 to 14 in the periodic table. Specific examples thereof include organic group-containing compounds such as carboxylates, alkoxy salts, organic sulfonates and β-diketonates, which contain at least one metal selected from the group consisting of titanium, zirconium, tin, antimony, cerium, germanium, zinc, cobalt, manganese, iron, aluminum, magnesium, calcium, strontium, sodium and potassium; inorganic compounds such as oxides and halides of the above-described metals; and mixtures of these compounds. Because of the above-described reason, these catalyst components may be contained in the polyester starting material derived from a biomass resource. In this a case, the starting material does not have to be particularly purified and may be used as-is in the form of a starting material containing a metal. However, depending on the polyester to be produced, there are cases where the lower is the content of a metal atom of the Group 1 such as sodium or potassium in the polyester starting material, the easier is it to produce a polyester having a high polymerization degree. In such a case, a starting material which is purified to such an extent that it does not substantially contain a metal element of the Group 1 is suitably employed.

Among the above-described polymerization catalysts, metal compounds containing titanium, zirconium, germanium, zinc, aluminum, magnesium or calcium and mixtures of these metal compounds are preferred. Thereamong, titanium compounds, zirconium compounds and germanium compounds are particularly preferred. Further, the catalyst is preferably in the form of a liquid or a compound soluble to an ester low polymer or polyester at the time of polymerization because the polymerization rate is increased when the catalyst is in a molten or dissolved state at the time of polymerization.

As the titanium compound, tetraalkyl titanate is preferred, and specific examples thereof include tetra-n-propyl titanate, tetraisopropyl titanate, tetra-n-butyl titanate, tetra-t-butyl titanate, tetraphenyl titanate, tetracyclohexyl titanate, tetrabenzyl titanate and mixed titanates thereof. In addition, titanium (oxy)acetylacetonate, titanium tetraacetylacetonate, titanium (diisopropoxide)acetylacetonate, titanium bis(ammonium lactate)dihydroxide, titanium bis(ethylacetoacetate)diisopropoxide, titanium (triethanolaminate)isopropoxide, polyhydroxytitanium stearate, titanium lactate, titanium triethanolaminate, butyl titanate dimer and the like can be suitably used as well. Moreover, titanium oxide and complex oxides containing titanium and silicon can also be suitably used.

Among these titanium compounds, tetra-n-propyl titanate, tetraisopropyl titanate, tetra-n-butyl titanate, titanium (oxy)acetylacetonate, titanium tetraacetylacetonate, titanium bis(ammonium lactate)dihydroxide, polyhydroxytitanium stearate, titanium lactate, butyl titanate dimer, titanium oxide and titania/silica complex oxides are preferred, and tetra-n-butyl titanate, titanium (oxy)acetylacetonate, titanium tetraacetylacetonate, polyhydroxytitanium stearate, titanium lactate, butyl titanate dimer and titania/silica complex oxides are more preferred. Further, tetra-n-butyl titanate, polyhydroxytitanium stearate, titanium (oxy)acetylacetonate, titanium tetraacetylacetonate and titania/silica complex oxides are particularly preferred.

Specific examples of the zirconium compounds include zirconium tetraacetate, zirconium acetate hydroxide, zirconium tris(butoxy)stearate, zirconyl diacetate, zirconium oxalate, zirconyl oxalate, zirconium potassium oxalate, polyhydroxyzirconium stearate, zirconium ethoxide, zirconium tetra-n-propoxide, zirconium tetraisopropoxide, zirconium tetra-n-butoxide, zirconium tetra-t-butoxide, zirconium tributoxyacetylacetonate and mixtures thereof. Further, zirconium oxide and complex oxides containing zirconium and silicon can also be suitably used.

Among these zirconium compounds, zirconyl diacetate, zirconium tris(butoxy)stearate, zirconium tetraacetate, zirconium acetate hydroxide, zirconium ammonium oxalate, zirconium potassium oxalate, polyhydroxyzirconium stearate, zirconium tetra-n-propoxide, zirconium tetraisopropoxide, zirconium tetra-n-butoxide and zirconium tetra-t-butoxide are preferred, and zirconyl diacetate, zirconium tetraacetate, zirconium acetate hydroxide, zirconium tris(butoxy)stearate, zirconium ammonium oxalate, zirconium tetra-n-propoxide and zirconium tetra-n-butoxide are more preferred. Further, zirconium tris(butoxy)stearate is particularly preferred since it allows a colorless polyester having a high polymerization degree to be easily obtained.

Specific examples of the germanium compounds include inorganic germanium compounds such as germanium oxide and germanium chloride; and organic germanium compounds such as tetraalkoxygermanium. From the standpoints of price, availability and the like, for example, germanium oxide, tetraethoxygermanium and tetrabutoxygermanium are preferred, and germanium oxide is particularly preferred.

In cases where a metal compound is used as the polymerization catalyst, when the amount of the catalyst is excessively large, not only is it economically disadvantageous, but also the thermal stability of the resulting polymer is reduced. On the other hand, when the amount of the catalyst is excessively small, the polymerization activity is decreased, so that the polymer becomes more likely to be decomposed during the production. Accordingly, the lower limit of the amount of the catalyst to be used is, in terms of the amount of the metal with respect to that of the resulting polyester, usually not less than 5 ppm, preferably not less than 10 ppm, while the upper limit thereof is usually not more than 30,000 ppm, preferably not more than 1,000 ppm, more preferably not more than 250 ppm, particularly preferably not more than 130 ppm.

<Polyester and Use Thereof>

A polyester produced by the method of the present invention is generally characterized in that the amount of terminal carboxylic acid, which markedly deteriorates the thermal stability of a polymer, is small; therefore, the polyester has characteristic features that it has excellent thermal stability and a reduction in the quality at the time of molding is thus small, that is, occurrence of side reactions such as breakage of the terminal group and main chain is limited at the time of melt molding. Accordingly, in a preferred polyester produced in the present invention, the number of terminal COOH groups is, although it varies depending on the polymerization degree of the polyester, usually not more than 100 equivalents/ton (hereinafter, may be abbreviated as “eq/ton”), preferably not more than 60 eq/ton, more preferably not more than 40 eq/ton, particularly preferably not more than 30 eq/ton. Meanwhile, when the amount of terminal carboxyl group is excessively small, the polymerization rate becomes extremely slow, so that a polymer having a high-polymerization degree cannot be produced. For this reason, the lower limit of the number of terminal COOH groups in the polyester is usually not less than 0.1 eq/ton, more preferably not less than 1 eq/ton.

It is usually preferred that the polyester produced in the present invention be one having limited coloration. The upper limit of the yellowness (Y.I. value) of the polyester is usually not higher than 50, preferably not higher than 30, more preferably not higher than 20, still more preferably not higher than 15, particularly preferably not higher than 10. Meanwhile, the lower limit thereof is not particularly restricted; however, it is usually not lower than −20, preferably not lower than −10, more preferably not lower than −5, particularly preferably not lower than −3, most preferably not lower than −1. A polyester showing a high Y.I. value has a drawback in that the use of a film, a sheet or the like thereof is restricted. Meanwhile, a polyester showing a low Y.I. value is a more preferred embodiment; however, it is economically disadvantageous in that, for example, the production of such a polymer requires complex production processes as well as an extremely large investment in the equipments. In the present invention, the Y.I. value is measured by the method according to JIS K7105.

In the polyester produced in the present invention, from the standpoint of attaining practically sufficient mechanical characteristics, the reduced viscosity (ηsp/C) value is not less than 0.5, more preferably not less than 1.6, still more preferably not less than 2.0, particularly preferably not less than 2.3. From the standpoint of operability such as the easiness of recovering the resulting polyester after the polymerization reaction and the moldability thereof, the upper limit of the reduced viscosity (ηsp/C) value is usually not higher than 6.0, preferably not higher than 5.0, still more preferably not higher than 4.0.

In the present invention, the reduced viscosity is measured under the following measurement conditions.

[Conditions for Measuring Reduced Viscosity (ηsp/C)]

Viscosity tube: Ubbelohde's viscosity tube

Measuring temperature: 30° C.

Solvent: phenol/tetrachloroethane (1:1 weight ratio) solution

Polyester concentration: 0.5 g/d1

In the method of producing a polyester according to the present invention, a variety of additives, such as a heat stabilizer, an antioxidant, a nucleating agent, a flame retardant, an antistatic agent, a mold releasing agent and/or an ultraviolet absorber, may also be added to the reaction system at the time of performing polymerization or to the resulting polyester in such a range which does not adversely affect the properties of the polyester.

Further, in addition to the above-described various additives, at the time of molding, a reinforcing agent and a filler, such as a glass fiber, a carbon fiber, a titanium whisker, mica, talc, CaCO₃, TiO₂ and silica, may also be added to perform molding.

The polyester obtained by the production method of the present invention has excellent heat resistance and color tone as well as excellent hydrolysis resistance and biodegradability and can be produced inexpensively; therefore, it is suitably used in a variety of film applications and applications of injection-molded articles.

A molded article can be produced by molding the polyester obtained by the production method of the present invention. As a molding method, any conventional method can be employed. Examples of the molded article which can be obtained are shown below along with the applications thereof. Specific examples of the application include injection-molded articles (e.g., trays used for fresh foods, containers of fast foods and outdoor leisure products), extrusion-molded articles (e.g., films, sheets, fishing lines, fishing nets, vegetation nets and water-holding sheets) and blow-molded articles (e.g., bottles). In addition, the polyester can also be utilized in, for example, agricultural films, coating materials, fertilizer coating materials, laminated films, plates, stretched sheets, monofilaments, multifilaments, nonwoven fabrics, flat yarns, staples, crimped fibers, striated tapes, split yarns, composite fibers, blow bottles, foamed articles, shopping bags, trash bags, compost bags, cosmetic containers, detergent containers, bleach containers, ropes, tying materials, surgical sutures, sanitary cover stock materials, cooler boxes, cushioning films and synthetic papers.

EXAMPLES

The present invention will now be described in more detail by way of examples thereof; however, the present invention is not restricted thereto.

<Method of Quantifying Organic Acid>

The amount of organic acid was measured by quantitative analysis using HPLC under the following conditions.

Column: Ultron PS-80H (8.0 mm I.D.×300 mm), manufactured by Shinwa Chemical Industries Ltd.

Eluent: water (perchloric acid) (60% aqueous perchloric acid solution, 1.8 ml/1 L—H₂O)

Temperature: 60° C.

Detection: RI, UV (210 nm)

<Method of Quantifying Ammonium Ion>

The amount of ammonium ion was measured by quantitative analysis using ion chromatography under the following conditions.

Column: GL-IC-C75 (4.6 mm I.D.×150 mm)

Eluent: 3.5 mmol/L sulfuric acid

Column temperature: 40° C.

<Method of Quantifying Aromatic Carboxylic Acid>

In Experimental Examples 1 to 3, the amount of aromatic carboxylic acid was measured by quantitative analysis using HPLC under the following conditions. In Example 2 and Comparative Example 2, the measurement was carried out under the same conditions as in the above-described method of quantifying organic acid.

Column: Develosil C30-UG (3 μm, 4.6 mm I.D.×100 mm), manufactured by Nomura Chemical Co., Ltd.

Eluent: 0.02% aqueous formic acid solution, 1.0 mL/min

Temperature: 40° C.

Detector: UV (280 nm)

<Polymer Evaluation Method>

Yellow Index (Hereinafter, May be Abbreviated as “Y.I.”)

In accordance with the method prescribed in JIS K7105, a chip of the obtained polymer was placed in a cell and the Y.I. thereof was measured 4 times by a reflection method using Color Meter ZE-6000 (manufactured by Nippon Denshoku Industries Co., Ltd.). The average value thereof was used as the Y.I. value of the polymer.

Reduced Viscosity

The obtained polyester was dissolved in phenol/tetrachloroethane (1/1 (mass ratio) mixture) to a concentration of 0.5 g/dl. Then, in a 30° C. thermostat bath of the resulting solution, the time (t: seconds) required for a viscosity tube to fall was measured. Further, the time required for the viscosity tube to fall in the bath of the solvent alone (t₀: seconds) was measured to calculate the reduced viscosity at 30° C. (η_(sp)/C=(t−t₀)/t₀·C; C represents the concentration of the solution).

Amount of Terminal Carboxyl Group

The obtained polyester was dissolved in benzyl alcohol and the resulting solution was titrated with 0.1N NaOH to determine the amount of terminal carboxyl group as an equivalent amount of terminal acid group per 1×10⁶ g of the polyester.

Example 1

[Preparation of Brevibacterium flavum MJ233/ΔQsuB/PC-4/ΔLDH] (Preparation of QsuB-Disrupted Strain)

(A) Extraction of Genomic DNA from MJ233 Strain

In 10 mL of a seed culture medium [2 g of urea, 7 g of (NH₄)₂SO₄, 0.5 g of KH₂PO₄, 0.5 g of K₂HPO₄, 0.5 g of MgSO₄.7H₂O, 6 mg of FeSO₄.7H₂O, 6 mg of MnSO₄.4-5H₂O, 200 μg of biotin, 100 μg of thiamine, 1 g of yeast extract, 1 g of casamino acid and 20 g of glucose; dissolved in 1 L of distilled water], the Brevibacterium flavum MJ-233 strain was cultured until the late stage of logarithmic growth phase, and the resulting bacterial cells were collected by centrifugation (10,000 g, 5 minutes). The thus obtained bacterial cells were suspended in 0.15 mL of a 10 mM NaCl/20 mM Tris buffer (pH 8.0)/1 mM EDTA.2Na solution containing lysozyme at a concentration of 10 mg/mL. Then, proteinase K was added to the thus obtained suspension to a final concentration of 100 μg/mL and the resultant was incubated at 37° C. for 1 hour. Thereafter, sodium dodecyl sulfate was further added to a final concentration of 0.5% and the resultant was incubated at 50° C. for 6 hours to perform bacteriolysis. To the resulting lysate, an equivalent amount of a phenol/chloroform solution was added. After gently shaking the resultant at room temperature for 10 minutes, the whole amount thereof was centrifuged (5,000 G, 20 minutes, 10 to 12° C.) and a supernatant fraction was recovered. Then, after adding sodium acetate to the thus recovered fraction to a concentration of 0.3 M, a double amount of ethanol was further added and the resultant was mixed. The resulting mixture was centrifuged (15,000 G, 2 minutes) to recover precipitates, which were then washed with 70% ethanol and air-dried. To the thus obtained DNA, 5 mL of a 10 mM Tris buffer (pH 7.5)/1 mM EDTA.2Na solution was added, and the resultant was left to stand at 4° C. overnight and then used as a template DNA in the later PCR.

(B) Construction of Plasmid for Disruption of QsuB Gene

A DNA fragment of the qsuB gene originated from the Brevibacterium flavum MJ233 strain in which an internal sequence thereof was deleted was obtained by performing crossover PCR using the DNA prepared in the above-described (A) as a template and synthetic DNAs (SEQ ID NOs:1, 2, 3 and 4) which were designed based on a sequence of the vicinity of the qsuB gene of the Corynebacterium glutamicum ATCC13032 strain whose entire genomic sequence has been reported (GenBank Accession No. BA000036). PCR of the DNA fragment containing the 5′-end region of the qsuB gene was performed using the synthetic DNAs shown in SEQ ID NOs:1 and 2 as primers, while PCR of the DNA fragment containing the 3′-end region of the qsuB gene was performed using the synthetic DNAs shown in SEQ ID NOs:3 and 4 as primers. The composition of the reaction solution was as follows: 1 μL of the template DNA, 0.5 μL of PfxDNA polymerase (manufactured by Invitrogen Corporation), 1-fold concentration of the attached buffer, 0.4 μM of each primer, 1 mM MgSO₄ and 0.2 μM dNTPs were mixed and the total volume was adjusted to 50 μL. The reaction temperature conditions were as follows: a DNA thermal cycler (PTC-200, manufactured by MJ Research Inc.) was used and a cycle of 94° C. for 15 seconds, 55° C. for 30 seconds and 68° C. for 45 seconds was repeated 35 times. It is noted here, however, that the reaction solution was retained at 94° C. for 2 minutes in the first cycle and at 68° C. for 3 minutes in the final cycle. Then, PCR was further carried out using the resulting two amplification products as templates and the synthetic DNAs shown in SEQ ID NOs:1 and 4 as primers. Here, the composition of the reaction solution was as follows: 1 μL of the template DNAs, 0.5 μL of PfxDNA polymerase (manufactured by Invitrogen Corporation), 1-fold concentration of the attached buffer, 0.4 μM of each primer, 1 mM MgSO₄ and 0.2 μM dNTPs were mixed and the total volume was adjusted to 50 μL. The reaction temperature conditions were as follows: a DNA thermal cycler (PTC-200, manufactured by MJ Research Inc.) was used and a cycle of 94° C. for 15 seconds, 55° C. for 30 seconds and 68° C. for 1 minute and 20 seconds was repeated 35 times. It is noted here, however, that the reaction solution was retained at 94° C. for 2 minutes in the first cycle and at 68° C. for 3 minutes in the final cycle. The thus obtained DNA fragment in which the internal sequence of the qsuB gene was deleted was purified using ChargeSwitch PCR Clean-Up Kit (manufactured by Invitrogen Corporation) and then digested with restriction enzymes XhoI and SacI. After separating the resulting DNA fragment of about 1.2 kb by 0.9% agarose gel electrophoresis (SeaKem GTG agarose; manufactured by FMC BioProducts), the DNA fragment was detected by visualizing it with ethidium bromide staining and then recovered from the gel using Zymoclean Gel DNA Recovery Kit (manufactured by Zymo Research Corporation). The thus obtained DNA was mixed with a DNA prepared by digesting the plasmid pKMB1 (JP 2005-95169A) with restriction enzymes XhoI and SacI, and these DNAs were ligated with each other using Ligation Kit ver. 2 (manufactured by Takara Bio Inc.). Using the thus obtained plasmid DNA, Escherichia coli (DH5α strain) was transformed and then spread onto an LB agar medium containing 50 μg/mL of kanamycin and 50 μg/mL of X-Gal. A clone which formed a white colony on this medium was cultured in a liquid medium by a conventional method and a plasmid DNA was then purified. The thus obtained plasmid DNA was digested with restriction enzymes XhoI and SacI. As a result, an insert fragment of about 1.2 kb was detected and this was named “pQsuB1”. The construction process of the pQsuB1 is shown in FIG. 3.

(C) Preparation of QsuB-Disrupted Strain

As a sample strain for preparing a QsuB-disrupted strain, the Brevibacterium flavum MJ233/PC-4/ΔLDH strain prepared in the later-described Reference Example 1 was employed. A plasmid DNA to be used for transformation of the Brevibacterium flavum MJ233/PC-4/ΔLDH strain was prepared from Escherichia coli JM110 strain which was transformed with the pQsuB1 plasmid constructed in the above-described (B). The transformation of the Brevibacterium flavum MJ233/PC-4/ΔLDH strain was carried out by an electric pulse method (Vertes A. A., Inui M., Kobayashi M., Kurusu Y. and Yukawa H., Res. Microbiol., 1993, vol. 144 (3), p 181-185), and the resulting transformant was spread onto an LBG agar medium containing 50 μg/mL of kanamycin [10 g of tryptone, 5 g of yeast extract, 5 g of NaCl, 20 g of glucose and 15 g of ager; dissolved in 1 L of distilled water]. In the strain that grew on this medium, since the pQsuB1 is a plasmid which cannot be replicated in the cells of the Brevibacterium flavum MJ233 strain, as a result of homologous recombination between the qsuB gene of the plasmid and the qsuB gene on the genome of the Brevibacterium flavum MJ-233 strain, a kanamycin-resistant gene originated from the plasmid is expected to have been inserted in the genome. Whether or not the kanamycin-resistant strain obtained in this manner carries such gene derived by homologous recombination between the qsuB gene existing on its genome and the qsuB gene existing on the plasmid pQsuB1 was verified by performing colony PCR using the synthetic DNAs shown in SEQ ID NOs:1 and 5 and SEQ ID NOs:4 and 6 as primers. The template DNA was prepared in the form of a supernatant which was obtained by suspending the formed colonies in 50 μL of sterilized water and boiling the resulting suspension for 5 minutes. The composition of the reaction solution was as follows: 1 μL of the template DNA, 0.2 μL of Ex-Taq DNA polymerase (manufactured by Takara Bio Inc.), 1-fold concentration of the attached buffer, 0.2 μM of each primer and 0.2 μM dNTPs were mixed and the total volume was adjusted to 20 μL. The reaction temperature conditions were as follows: a DNA thermal cycler (PTC-200, manufactured by MJ Research Inc.) was used and a cycle of 98° C. for 10 seconds, 55° C. for 20 seconds and 72° C. for 2 minutes was repeated 35 times. It is noted here, however, that the reaction solution was retained at 95° C. for 2 minutes in the first cycle and at 72° C. for 3 minutes in the final cycle. As a result of analyzing the kanamycin-resistant strain by the above-described method, a strain which yields a PCR amplification product of 1,256 bp with the combination of SEQ ID NOs:1 and 5 and a PCR amplification product of 1,866 bp with the combination of SEQ ID NOs:4 and 6 was selected, and this strain was named “Brevibacterium flavum MJ233/ΔQsuB/PC-4/ΔLDH”.

(Evaluation of Growth of QsuB-Disrupted Strain on Synthetic Medium)

A MM medium [4 g of urea, 14 g of (NH₄)₂SO₄, 0.5 g of KH₂PO₄, 0.5 g of K₂HPO₄, 0.5 g of MgSO₄.7H₂O, 20 mg of FeSO₄.7H₂O, 20 mg of MnSO₄.H₂O, 200 μg of D-biotin and 200 μg of thiamine hydrochloride; dissolved in 1 L of distilled water] in an amount of 100 mL was placed in a 500-mL Erlenmeyer flask and heat-sterilized at 120° C. for 20 minutes. The medium was then cooled to room temperature and 6 mL of 50% aqueous glucose solution which had been sterilized in advance and 50 μL of filter-sterilized 5% aqueous kanamycin solution were added thereto. The Brevibacterium flavum MJ233/ΔQsuB/PC-4/ΔLDH strain was inoculated to the resulting medium to an absorbance (OD₆₆₀) of 1.0 and cultured at 30° C. with stirring at 160 rpm. At 1.5 hours, 3.1 hours, 5.0 hours, 7.0 hours, 9.0 hours, 11.0 hours and 23.5 hours after the start of the culture, the absorbance (OD₆₆₀) of the culture medium was measured. The measurement results are shown in Table 1.

Reference Example 1

[Preparation of Brevibacterium flavum MJ233/PC-4/ΔLDH Strain]

(Preparation of Pyruvate Carboxylase (PC)-Enhanced Strain)

(A) Extraction of Genomic DNA from Brevibacterium flavum MJ233 Strain

In 10 mL of A medium [2 g of urea, 7 g of (NH₄)₂SO₄, 0.5 g of KH₂PO₄, 0.5 g of K₂HPO₄, 0.5 g of MgSO₄.7H₂O, 6 mg of FeSO₄.7H₂O, 6 mg of MnSO₄.4-5H₂O, 200 μg of biotin, 100 μg of thiamine, 1 g of yeast extract, 1 g of casamino acid and 20 g of glucose; dissolved in 1 L of distilled water], Brevibacterium flavum MJ-233 strain was cultured until the late stage of logarithmic growth phase, and the resulting bacterial cells were collected by centrifugation (10,000 g, 5 minutes). The thus obtained bacterial cells were suspended in 0.15 mL of a 10 mM NaCl/20 mM Tris buffer (pH 8.0)/1 mM EDTA.2Na solution containing lysozyme at a concentration of 10 mg/mL. Then, proteinase K was added to the thus obtained suspension to a final concentration of 100 μg/mL and the resultant was incubated at 37° C. for 1 hour. Thereafter, sodium dodecyl sulfate was further added to a final concentration of 0.5% and the resultant was incubated at 50° C. for 6 hours to perform bacteriolysis. To the resulting lysate, an equivalent amount of a phenol/chloroform solution was added. After gently shaking the resultant at room temperature for 10 minutes, the whole amount thereof was centrifuged (5,000 G, 20 minutes, 10 to 12° C.) and a supernatant fraction was recovered. Then, after adding sodium acetate to the thus recovered fraction to a concentration of 0.3 M, a double amount of ethanol was further added and the resultant was mixed. The resulting mixture was centrifuged (15,000 G, 2 minutes) to recover precipitates, which were then washed with 70% ethanol and air-dried. To the thus obtained DNA, 5 mL of a 10 mM Tris buffer (pH 7.5)/1 mM EDTA.2Na solution was added, and the resultant was left to stand at 4° C. overnight and then used as a template DNA in the later PCR.

(B) Construction of Plasmid for Substitution of PC Gene Promoter

A DNA fragment of the N-terminal region of the pyruvate carboxylase gene originated from the Brevibacterium flavum MJ233 strain was obtained by performing PCR using the DNA prepared in the above-described (A) as a template and synthetic DNAs (SEQ ID NOs:19 and 20) which were designed based on the sequence of the pyruvate carboxylase gene of the Corynebacterium glutamicum ATCC 13032 strain whose entire genomic sequence has been reported (GenBank Accession No. BA000036). It is noted here that the DNA shown in SEQ ID NO:19 was phosphorylated at the 5′-end. The composition of the reaction solution was as follows: 1 μL of the template DNA, 0.2 μL of PfxDNA polymerase (manufactured by Invitrogen Corporation), 1-fold concentration of the attached buffer, 0.3 μM of each primer, 1 mM MgSO₄ and 0.25 μM dNTPs were mixed and the total volume was adjusted to 20 μL. The reaction temperature conditions were as follows: a DNA thermal cycler (PTC-200, manufactured by MJ Research Inc.) was used and a cycle of 94° C. for 20 seconds, 60° C. for 20 seconds and 72° C. for 1 minute was repeated 35 times. It is noted here, however, that the reaction solution was retained at 94° C. for 1 minute and 20 seconds in the first cycle and at 72° C. for 4 minutes in the final cycle. The resulting amplification products were verified by separating them by 0.75% agarose gel electrophoresis (SeaKem GTG agarose; manufactured by FMC BioProducts) and then visualizing with ethidium bromide staining. As a result, a fragment of about 0.9 kb was detected. The DNA fragment of interest was recovered from the gel using QIAQuick Gel Extraction Kit (manufactured by QIAGEN) as a PC gene N-terminal fragment.

Meanwhile, a TZ4 promoter fragment which is originated from the Brevibacterium flavum MJ233 strain and constitutively highly expressed was prepared by performing PCR using the plasmid pMJPC1 (JP 2005-95169A) as a template and the synthetic DNAs shown in SEQ ID NOs:21 and 22. It is noted here that the DNA shown in SEQ ID NO:22 was phosphorylated at the 5′-end. The composition of the reaction solution was as follows: 1 μL of the template DNA, 0.2 μL of PfxDNA polymerase (manufactured by Invitrogen Corporation), 1-fold concentration of the attached buffer, 0.3 μM of each primer, 1 mM MgSO₄ and 0.25 μM dNTPs were mixed and the total volume was adjusted to 20 μL. The reaction temperature conditions were as follows: a DNA thermal cycler (PTC-200, manufactured by MJ Research Inc.) was used and a cycle of 94° C. for 20 seconds, 60° C. for 20 seconds and 72° C. for 30 seconds was repeated 25 times. It is noted here, however, that the reaction solution was retained at 94° C. for 1 minute and 20 seconds in the first cycle and at 72° C. for 3 minutes in the final cycle. The resulting amplification products were verified by separating them by 1.0% agarose gel electrophoresis (SeaKem GTG agarose; manufactured by FMC BioProducts) and then visualizing with ethidium bromide staining. As a result, a fragment of about 0.5 kb was detected. The DNA fragment of interest was recovered from the gel using QIAQuick Gel Extraction Kit (manufactured by QIAGEN) as a TZ4 promoter fragment.

The thus obtained PC gene N-terminal fragment and TZ4 promoter fragment were mixed and ligated with each other using Ligation Kit ver. 2 (manufactured by Takara Shuzo Co., Ltd.). Then, the resultant was digested with a restriction enzyme PstI and the resulting fragments were separated by 1.0% agarose gel electrophoresis (SeaKem GTG agarose; manufactured by FMC BioProducts). A DNA fragment of about 1.0 kb was recovered by using QIAQuick Gel Extraction Kit (manufactured by QIAGEN) as TZ4 promoter::PC gene N-terminal fragment. Further, this DNA fragment was mixed with a DNA prepared by digesting Escherichia coli plasmid pHSG299 (manufactured by Takara Shuzo Co., Ltd.) with PstI and they were ligated with each other using Ligation Kit ver. 2 (manufactured by Takara Shuzo Co., Ltd.). Using the thus obtained plasmid DNA, Escherichia coli (DH5α strain) was transformed. The recombinant Escherichia coli obtained in this manner was then spread onto an LB agar medium containing 50 μg/mL of kanamycin and 50 μg/mL of X-Gal. A clone which formed a white colony on this medium was cultured in a liquid medium by a conventional method and a plasmid DNA was then purified. The thus obtained plasmid DNA was digested with a restriction enzyme PstI. As a result, an insert fragment of about 1.0 kb was detected and this plasmid was named “pMJPC17.1”.

A DNA fragment of a 5′-upstream region of the pyruvate carboxylase gene originated from the Brevibacterium flavum MJ233 strain was obtained by performing PCR using the DNA prepared in the above-described (A) as a template and synthetic DNAs (SEQ ID NOs:23 and 24) which were designed based on the sequence of the pyruvate carboxylase gene of the Corynebacterium glutamicum ATCC13032 strain whose entire genomic sequence has been reported (GenBank Accession No. BA000036). The composition of the reaction solution was as follows: 1 μL of the template DNA, 0.2 μL of PfxDNA polymerase (manufactured by Invitrogen Corporation), 1-fold concentration of the attached buffer, 0.3 μM of each primer, 1 mM MgSO₄ and 0.25 μM dNTPs were mixed and the total volume was adjusted to 20 μL. The reaction temperature conditions were as follows: a DNA thermal cycler (PTC-200, manufactured by MJ Research Inc.) was used and a cycle of 94° C. for 20 seconds, 60° C. for 20 seconds and 72° C. for 30 seconds was repeated 35 times. It is noted here, however, that the reaction solution was retained at 94° C. for 1 minute and 20 seconds in the first cycle and at 72° C. for 5 minutes in the final cycle. The resulting amplification products were verified by separating them by 1.0% agarose gel electrophoresis (SeaKem GTG agarose; manufactured by FMC BioProducts) and then visualizing with ethidium bromide staining. As a result, a fragment of about 0.7 kb was detected. The DNA fragment of interest was recovered from the gel using QIAQuick Gel Extraction Kit (manufactured by QIAGEN). The thus recovered DNA fragment was phosphorylated at the 5′-end with T4 Polynucleotide Kinase (manufactured by Takara Shuzo Co., Ltd.) and then ligated to the SmaI site of the Escherichia coli vector pUC 119 (manufactured by Takara Shuzo Co., Ltd.) using Ligation Kit ver. 2 (manufactured by Takara Shuzo Co., Ltd.). Using the thus obtained plasmid DNA, Escherichia coli (DH5α strain) was transformed. The recombinant Escherichia coli obtained in this manner was then spread onto an LB agar medium containing 50 μg/mL of ampicillin and 50 μg/mL of X-Gal. A clone which formed a white colony on this medium was cultured in a liquid medium by a conventional method and a plasmid DNA was then purified. Thereafter, the thus obtained plasmid DNA was subjected to PCR using the synthetic DNAs shown in SEQ ID NOs:25 and 24 as primers. The composition of the reaction solution was as follows: 1 ng of the above-described plasmid, 0.2 μL of Ex-Taq DNA polymerase (manufactured by Takara Shuzo Co., Ltd.), 1-fold concentration of the attached buffer, 0.2 μM of each primer and 0.25 μM dNTPs were mixed and the total volume was adjusted to 20 μL. The reaction temperature conditions were as follows: a DNA thermal cycler (PTC-200, manufactured by MJ Research Inc.) was used and a cycle of 94° C. for 20 seconds, 60° C. for 20 seconds and 72° C. for 50 seconds was repeated 20 times. It is noted here, however, that the reaction solution was retained at 94° C. for 1 minute and 20 seconds in the first cycle and at 72° C. for 5 minutes in the final cycle. As a result of verifying the presence or absence of inserted DNA fragment in this manner, a plasmid which was found to contain an amplification product of about 0.7 kb was selected and named “pMJPC5.1”.

Then, the thus obtained plasmids pMJPC17.1 and pMJPC5.1 were each digested with an enzyme XbaI. Thereafter, the resultants were mixed and ligated using Ligation Kit ver. 2 (manufactured by Takara Shuzo Co., Ltd.). Then, the resultant was digested with restriction enzymes SacI and SphI and the resulting fragments were separated by 0.75% agarose gel electrophoresis (SeaKem GTG agarose; manufactured by FMC BioProducts). A DNA fragment of about 1.75 kb was recovered by using QIAQuick Gel Extraction Kit (manufactured by QIAGEN). The thus obtained DNA fragment, in which the TZ4 promoter was inserted between the 5′-upstream region and the N-terminal region of the PC gene, was mixed with a DNA prepared by digesting the plasmid pKMB1 (JP 2005-95169A) containing sacB gene with restriction enzymes SacI and SphI, and these DNAs were ligated with each other using Ligation Kit ver. 2 (manufactured by Takara Shuzo Co., Ltd.). Using the thus obtained plasmid DNA, Escherichia coli (DH5α strain) was transformed. The recombinant Escherichia coli obtained in this manner was then spread onto an LB agar medium containing 50 μg/mL of kanamycin and 50 μg/mL of X-Gal. A clone which formed a white colony on this medium was cultured in a liquid medium by a conventional method and a plasmid DNA was then purified. The thus obtained plasmid DNA was digested with restriction enzymes SacI and SphI. As a result, an insert fragment of about 1.75 kb was detected and this plasmid was named “pMJPC17.2” (FIG. 2).

(C) Preparation of PC-Enhanced Strain

A plasmid DNA to be used for transformation of the Brevibacterium flavum MJ233/ΔLDH (lactate dehydrogenase gene-disrupted strain: JP 2005-95169A) was prepared once again from Escherichia coli JM110 strain which was transformed with the plasmid DNA of pMJPC17.2 by a calcium chloride method (Journal of Molecular Biology, 53, p 159, 1970). The transformation of the Brevibacterium flavum MJ233/ΔLDH strain was carried out by an electric pulse method (Res. Microbiol., vol. 144, p. 181-185, 1993), and the resulting transformant was spread onto an LBG agar medium containing 25 μg/mL of kanamycin [10 g of tryptone, 5 g of yeast extract, 5 g of NaCl, 20 g of glucose and 15 g of ager; dissolved in 1 L of distilled water]. In the strain that grew on this medium, since the pMJPC17.2 is a plasmid which cannot be replicated in the cells of the Brevibacterium flavum MJ233 strain, as a result of homologous recombination between the PC gene of the plasmid and the PC gene on the genome of the Brevibacterium flavum MJ233 strain, a kanamycin-resistant gene and a sacB gene that are originated from the plasmid are expected to have been inserted in the genome. Then, the above-described homologous recombinant strain was cultured in a liquid LBG medium containing 25 μg/mL of kanamycin. This culture solution was then, in an amount corresponding to about 1,000,000 cells, spread onto 10% sucrose-containing LBG medium. As a result, several tens of strains, which were believed to have become sucrose-insensitive due to the loss of sacB gene caused by the second homologous recombination, were obtained. These strains obtained in this manner included those in which the TZ4 promoter originated from pMJPC17.2 was inserted in the upstream of the PC gene, as well as those which were converted back to be of a wild-type. Whether the PC gene is of a promoter-substituted type or a wild type can be easily verified by directly subjecting cells obtained by culturing in a liquid LBG medium to PCR and then detecting the PC gene. When the TZ4 promoter and the PC gene are analyzed by using the primers for PCR amplification (SEQ ID NOs: 26 and 27), a DNA fragment of 678 bp should be observed for the promoter-substituted type. As a result of analyzing the strain which was transformed to be sucrose-insensitive by the above-described method, a strain inserted with the TZ4 promoter was selected and this strain was named “Brevibacterium flavum MJ233/PC-4/ΔLDH”.

(D) Measurement of Pyruvate Carboxylase Activity

The transformed Brevibacterium flavum MJ233/PC-4/ΔLDH strain obtained in the above-described (C) was cultured overnight in 100 mL of A medium containing 2% glucose. After recovering the resulting bacterial cells, the cells were washed with 50 mL of 50 mM potassium phosphate buffer (pH 7.5) and then resuspended in 20 mL of buffer having the same composition. This suspension was homogenized by using Sonifier 350 (manufactured by Branson Ultrasonics Corporation) and centrifuged to obtain a supernatant as a cell-free extract. Using the thus obtained cell-free extract, the activity of pyruvate carboxylase was measured. The measurement of the enzyme activity was carried out by allowing a reaction to take place at 25° C. in a reaction solution containing 100 mM Tris/HCl buffer (pH 7.5), 0.1 mg/10 ml biotin, 5 mM magnesium chloride, 50 mM sodium bicarbonate, 5 mM sodium pyruvate, 5 mM sodium adenosine triphosphate, 0.32 mM NADH, 20 units/1.5 ml malate dehydrogenase (manufactured by Wako Pure Chemical Industries, Ltd.; originated from yeast) and the enzyme. Here, “1 U” was defined as an amount of the enzyme required for catalyzing a 1-μmol reduction of NADH in a period of 1 minute. The cell-free extract in which the expression of pyruvate carboxylase was enhanced had a specific activity of 0.1 U/mg-protein. It is noted here that the cells obtained by culturing the parent strain, MJ233/ΔLDH strain, in the same manner had a specific activity of below the detection limit of this enzyme activity measuring method.

Comparative Example 1

(Evaluation of Growth on Synthetic Medium)

The evaluation was carried out in the same manner as in Example 1 except that the Brevibacterium flavum MJ233/PC-4/ΔLDH strain was used in place of the Brevibacterium flavum MJ233/ΔQsuB/PC-4/ΔLDH strain. It is noted here that kanamycin was not added during the culture. In the same manner as in Example 1, the absorbance (OD₆₆₀) of the culture medium was measured at 1.5 hours, 3.1 hours, 5.0 hours, 7.0 hours, 9.0 hours, 11.0 hours and 23.5 hours after the start of the culture. The measurement results are shown in Table 1.

TABLE 1 Culturing time Example 1 Comparative Example 1 [h] OD₆₆₀ OD₆₆₀ 1.5 1.16 1.30 3.1 1.82 2.03 5.0 2.98 3.42 7.0 4.55 4.85 9.0 6.88 7.20 11.0 8.27 8.29 23.5 9.01 8.75

From the results shown in Table 1, it was confirmed that the disruption of the qsuB gene does not adversely affect the growth on the synthetic medium.

Example 2

(Production of Succinic Acid by QsuB-Disrupted Strain)

A medium [4 g of urea, 14 g of (NH₄)₂SO₄, 0.5 g of KH₂PO₄, 0.5 g of K₂HPO₄, 0.5 g of MgSO₄.7H₂O, 20 mg of FeSO₄.7H₂O, 20 mg of MnSO₄.H₂O, 200 μg of D-biotin, 200 μg of thiamine hydrochloride, 1 g of yeast extract and 1 g of casamino acid; dissolved in 1 L of distilled water] in an amount of 100 mL was placed in a 500-mL Erlenmeyer flask and heat-sterilized at 120° C. for 20 minutes. The medium was then cooled to room temperature and 8 mL of 50% aqueous glucose solution which had been sterilized in advance and 50 μL of filter-sterilized 5% aqueous kanamycin solution were added thereto. The QsuB-disrupted strain (Brevibacterium flavum MJ233/ΔQsuB/PC-4/ΔLDH) prepared in Example 1 was inoculated to the resulting medium to an absorbance (OD₆₆₀) of 1.0 and cultured at 30° C.

At 12 hours after the start of the culture, 3.16 g of ammonium bicarbonate was added and allowed to react with the cells with the mouth of the Erlenmeyer flask being tightly closed with a parafilm. After the reaction, the cells were removed by centrifugation at 10,000 G for 5 minutes and the organic acid concentration of the resulting supernatant was analyzed by the above-described measurement method. As a result, the amount of protocatechuic acid generated in the culture medium after the reaction was found to be 12 ppm with respect to the amount of the generated succinic acid. The succinic acid concentration of the culture medium after the reaction was 14.3 g/L.

Comparative Example 2

The evaluation was carried out in the same manner as in Example 2 except that the pyruvate carboxylase (PC)-enhanced strain (Brevibacterium flavum MJ233/PC-4/ΔLDH) prepared in Reference Example 1 was used in place of the QsuB-disrupted strain (Brevibacterium flavum MJ233/ΔQsuB/PC-4/ΔLDH) prepared in Example 1. It is also noted here that kanamycin was not added during the culture.

As a result of analyzing the organic acid concentration of the resulting culture medium in the same manner as in Example 2, the amount of protocatechuic acid generated in the culture medium after the reaction was found to be 564 ppm with respect to the amount of the generated succinic acid. The succinic acid concentration of the culture medium after the reaction was 14.5 g/L.

From these results, it was confirmed that the disruption of the qsuB gene markedly reduces the by-production of protocatechuic acid.

Experimental Example 1

[Model Experiment: Production of Polymer Using Succinic Acid Obtained in

Comparative Example 2

(Preparation of Succinic Acid-Containing Solution A)

A food additive-grade succinic acid (manufactured by Kawasaki Kasei Chemical Ltd.) and protocatechuic acid (manufactured by Wako Pure Chemical Industries, Ltd.) were dissolved in hot water of 80° C. to prepare a solution A having a succinic acid concentration of 35% by weight and a protocatechuic acid concentration of 197 ppm (succinic acid: 564 ppm).

(Crystallization)

The thus obtained succinic acid-containing solution A was stored in an aqueous succinic acid solution feed tank. The succinic acid-containing solution A was then fed to a crystallization bath, whose jacket temperature was controlled at 80° C. by a program-controlled circulation thermostat bath, by means of a stock solution feed pump until the liquid level reached a prescribed point. Once the liquid level reached the prescribed point, while stirring the solution with paddle blades at a rate of 500 rotation/minutes, the hot water being supplied to the jacket of the crystallization bath was cooled to 20° C. over a period of about one hour, thereby lowering the temperature inside the crystallization bath to 20° C. After the crystallization bath was cooled to 20° C., while maintaining this temperature, the stirring was continued for another one hour.

Thereafter, while controlling the temperature of the cold water being passed through the jacket so that the temperature inside the crystallization bath was maintained at 20° C., the succinic acid-containing solution A was continuously fed at a rate of 250 ml/minute and a solid succinic acid-containing slurry was intermittently removed into a slurry recovery tank once every 15 minutes or so in order to keep the volume of the succinic acid-containing slurry in the crystallization bath almost constant. The removed succinic acid-containing slurry was vacuum-filtered to be separated into a succinic acid wet cake and a crystallization mother liquor every time the slurry was removed.

This continuous crystallization operation was continued for 24 hours and succinic acid wet cakes that were obtained after 6 hours or later from the start of the continuous crystallization operation were recovered. The thus recovered succinic acid wet cakes were suspended and washed in a 5-times weight of 10° C. cold water. Thereafter, the resulting slurry was vacuum-filtered to obtain a succinic acid wet cake. This wet cake was then vacuum-dried at 80° C. to recover succinic acid.

The thus obtained succinic acid was dissolved in 80° C. hot water to a succinic acid concentration of 35% by weight and the resulting solution was once again subjected to continuous crystallization for 7 hours by the above-described crystallization operation. Succinic acid wet cakes that were obtained between 6 and 7 hours in the continuous crystallization operation were suspended and washed in a 5-times weight of 10° C. cold water. Thereafter, the resulting slurry was vacuum-filtered to obtain a succinic acid wet cake. This wet cake was then vacuum-dried at 80° C. to recover succinic acid in an amount of 55 g. As a result of quantifying the aromatic carboxylic acid contained in the thus obtained succinic acid, it was found that the succinic acid contained 3.6 ppm of protocatechuic acid.

(Production of Polymer)

To a reaction vessel equipped with a stirring device, a nitrogen inlet, a heating apparatus, a thermometer and a pressure reduction vent, 100 parts by weight of the succinic acid obtained by the above-described crystallization operation was fed as a starting material along with 99.2 parts by weight of industrial-grade 1,4-butanediol (manufactured by Mitsubishi Chemical Corporation) and 0.38 parts by weight of malic acid (a total amount of 0.33 mol % with respect to the amount of the succinic acid), and the inside of the system was replaced to be a nitrogen atmosphere with nitrogen under reduced pressure. Then, with stirring, the inside of the system was heated to 230° C. over a period of 1 hour and then reaction was performed at this temperature for 1 hour. To this reaction solution, a catalyst solution prepared by the below-described method was added in such an amount that the amount of titanium atom became 50 ppm with respect to the amount of the resulting polyester theoretically calculated based on the amount of the starting material used.

To a 500-cm³ eggplant-shaped glass flask equipped with a stirring device, 62.0 g of magnesium acetate tetrahydrate was placed and 250 g of anhydrous ethanol (purity: not less than 99% by weight) was added thereto. Further, 35.8 g of ethyl acid phosphate (mixed weight ratio of monoester body and diester body=45:55) was added and the resulting mixture was stirred at 23° C. After 15 minutes, complete dissolution of magnesium acetate was confirmed and then 75.0 g of tetra-n-butyl titanate was added. The resulting mixture was stirred for another 10 minutes to obtain a uniform mixed solution. The thus obtained mixed solution was transferred to a 1,000-cm³ eggplant-shaped flask, which was then placed in a 60° C. oil bath to concentrate the mixed solution under reduced pressure using an evaporator. After 1 hour, most of ethanol was distilled out, and a semi-transparent viscous liquid was remained. Then, the temperature of the oil bath was raised to 80° C. to further concentrate the semi-transparent viscous liquid under a reduced pressure of 5 Ton. The viscous liquid gradually changed into the form of powder from the surface and completely powderized after 2 hours. Thereafter, the system was brought back to normal pressure using nitrogen and cooled to room temperature, thereby obtaining a pale yellow powder in an amount of 108 g. The thus obtained catalyst was subjected to metal element analysis and, as a result, it was found that the catalyst contained 10.3% by weight of titanium atom, 6.8% by weight of magnesium atom and 7.8% by weight of phosphorus atom and the molar ratios thereof were: T/P=0.77 and M/P=1.0. Furthermore, this powder-form catalyst was dissolved in 1,4-butanediol so that the titanium atom content became 34,000 ppm.

After adding the resulting catalyst solution, the inner temperature of the reaction vessel was slowly raised to 250° C. and, at the same time, the pressure was reduced to 0.06×10³ Pa over a period of 2 hours. The reaction was allowed to proceed for 2.5 hours at this reduced pressure, thereby producing a polyester. When the thus obtained polyester was evaluated in accordance with the above-described polymer evaluation method, it was found that the Y.I. value was 10, the reduced viscosity (ηsp/c) was 2.3 and the amount of terminal carboxyl group was 24 eq/ton.

Experimental Example 2

[Model Experiment (1): Production of Polymer Using Succinic Acid Obtained in Example 2]

(Preparation of Succinic Acid-Containing Solution B, Crystallization Thereof and Production of Polymer)

A food additive-grade succinic acid (manufactured by Kawasaki Kasei Chemical Ltd.) and protocatechuic acid (manufactured by Wako Pure Chemical Industries, Ltd.) were dissolved in hot water of 80° C. to prepare a solution B having a succinic acid concentration of 35% by weight and a protocatechuic acid concentration of 4.2 ppm (succinic acid: 564 ppm).

By performing the crystallization operation in the same manner as in Experimental Example 1 except that the thus obtained succinic acid-containing solution B was used, 54 g of succinic acid was recovered. As a result of quantifying the aromatic carboxylic acid contained in the thus obtained succinic acid, it was found that the succinic acid contained 0.1 ppm of protocatechuic acid.

Using the thus obtained succinic acid, a polyester was produced in the same manner as in Experimental Example 1. When this polyester was evaluated in accordance with the above-described polymer evaluation method, it was found that the Y.I. value was 5, the reduced viscosity (ηsp/c) was 2.3 and the amount of terminal carboxyl group was 24 eq/ton.

Experimental Example 3

[Model Experiment (2): Production of Polymer Using Succinic Acid Obtained in Example 2]

(Crystallization Using Succinic Acid-Containing Solution B and Production of Polymer)

The above-described succinic acid-containing solution B was stored in an aqueous succinic acid solution feed tank and subjected to continuous crystallization operation for 24 hours in the same manner as in Experimental Example 1. Succinic acid wet cakes that were obtained after 6 hours or later from the start of the continuous crystallization operation were recovered. The thus recovered succinic acid wet cakes were suspended and washed in a 5-times weight of 10° C. cold water. Thereafter, the resulting slurry was vacuum-filtered to obtain a succinic acid wet cake. This wet cake was then vacuum-dried at 80° C. to recover succinic acid. As a result of quantifying the aromatic carboxylic acid contained in the thus obtained succinic acid, it was found that the succinic acid contained 1 ppm of protocatechuic acid.

Using the thus obtained succinic acid, a polyester was produced in the same manner as in Experimental Example 1. When this polyester was evaluated in accordance with the above-described polymer evaluation method, it was found that the Y.I. value was 6, the reduced viscosity (ηsp/c) was 2.3 and the amount of terminal carboxyl group was 24 eq/ton.

Experimental Example 4

(Preparation of Succinic Acid-Containing Solution C, Crystallization Thereof and Production of Polymer)

A food additive-grade succinic acid (manufactured by Kawasaki Kasei Chemical Ltd.) and diammonium succinate (manufactured by Wako Pure Chemical Industries, Ltd.) were dissolved in hot water of 80° C. to prepare a solution C having a succinic acid concentration of 35% by weight and an ammonium ion concentration of 175 ppm (succinic acid: 5,000 ppm).

By performing the crystallization operation in the same manner as in Experimental Example 1 except that the thus obtained succinic acid-containing solution C was used, 60 g of succinic acid was recovered. As a result of quantifying the ammonium ion contained in the thus obtained succinic acid, it was found that the succinic acid contained ammonium ion in an amount of not higher than the detection limit (0.1 ppm).

Using the thus obtained succinic acid, a polyester was produced in the same manner as in Experimental Example 1. When this polyester was evaluated in accordance with the above-described polymer evaluation method, it was found that the Y.I. value was 5, the reduced viscosity (ηsp/c) was 2.3 and the amount of terminal carboxyl group was 24 eq/ton.

From the results of Experimental Examples 1 to 4, it is understood that the method of producing a polymer according to the present invention can reduce the coloration of resulting polymers.

Experimental Example 5

With reference to the method described in the below-listed References, uvitonic acid was synthesized. That is, 10 ml (2 mol) of an ammonia-ethanol solution was placed in a 100-ml three-necked flask and, while stirring the solution with a magnetic stirrer under N₂, 0.91 g (0.01 mol) of pyruvic acid was added thereto dropwise at room temperature. The resulting solution slightly generated heat and white precipitates were formed after a few minutes. Then, the thus obtained white precipitates were washed with ethanol.

REFERENCES

1. J. Org. Chem., 50, 1688 (1985)

2. Biochimie, 54, 115 (1972)

3. Vegetable Physiology and Agriculture

4. J. Org. Chem., 47, 1148 (1982)

Using a food additive-grade succinic acid (manufactured by Kawasaki Kasei Chemical Ltd.), polyesters were produced in the same manner as in the above-described Experimental Example 1, except that protocatechuic acid (manufactured by Wako Pure Chemical Industries, Ltd.) or the uvitonic acid produced by the above-described method was added in the amount shown in Table 2. The Y.I. value of the thus obtained respective polyesters was measured in accordance with the above-described polymer evaluation method. The measurement results are shown in Table 2 below.

TABLE 2 Concentration of protocatechuic acid with respect to the amount of succinic acid at the time of feeding (ppm) 0 10 57 Y.I. value 5 17 40 Concentration of uvitonic acid with respect to the amount of succinic acid at the time of feeding (ppm) 0 27 76 Y.I. value 5 10 17

From the above results, it is understood that protocatechuic acid and uvitonic acid, which are aromatic carboxylic acids, are substances that cause coloration of a polymer.

INDUSTRIAL APPLICABILITY

In general, succinic acid is produced from a petrochemically-derived material and used in a wide variety of applications. For these applications, succinic acid derived from a bioresource can also be preferably used in the same manner. For example, such succinic acid can be used as: a raw material of 1,4-butanediol, 2-pyrrolidine, succinimide, maleic anhydride, itaconic acid, aspartic acid, maleic acid, fumaric acid, hydroxysuccinimide, maleimide, 4-aminobutyric acid, γ-aminobutyric acid, tetrahydrofuran, acrylic acid, succinic esters such as dimethyl succinate and diethyl succinate, pyrrolidone, N-methylpyrrolidone and the like; as a starting material of polymer compounds such as polyester, polyurethane and polyamide and products thereof; a food additive such as an acidulant, a flavoring agent, a brewing agent or a processed food additive; a bubble bath component; a synthetic material or component of pharmaceuticals and agricultural chemicals such as plant growth inhibitors, herbicides, antibacterial agents, pesticides and mosquito attractants; a material or component of mouthwash, cosmetics and the like; a material or component of products that are used for photographs and printings; a material or component of adhesives and sealants such as high-temperature welding fluxes and alumite-treated surface adhesives; a material or component for metal processing such as powder nickel production, steel grinding bath, metal processing and washing solvents and binders for metal sintering; a material or component of solders and welding fluxes; a material or component of auxiliary agents that are used in the production of ceramics, inorganics and the like, such as production of a porous titanium oxide, production of boehmite, production of photocatalytic coating agents and production of ceramics; a material or component of detergents and the like; a material or component of bleaches and the like; a material or component of dyeing aids; a material or component of electrolyte solvents, plating solutions and the like; a material or component of deodorants, air cleaning agents and the like; a material of bioabsorbable compounds used for bioabsorbable surgical sutures and the like; a material or component of treatment agents, softeners and the like of textile goods; a material or component of fluxes, solvents and the like; a material or component of water-soluble paint solvents; a material or component of biodegradable resins; a material or component of sealants such as odor-free sealants; a material or component of anticorrosive agents that are used in coating of steel products, copper products and alloy metal products, freeze proofing, metal processing, lead for perchloric acid, boiler water treatment and the like; a material or component for synthesizing lubricants such as synthetic lubricants, lubricants for heat-resistant plastics and electrical contact lubricants; a material or component of solvent-removing washing agents and the like that used for resins, polymer materials and the like; a material or component of products that are used in the textile industry, dry cleaning and the like; a material or component of pigments, dyes, inks and the like that are used in, for example, ink solvents, deinking agents, automobile top-coating agents, insulating varnishes, powder paints, inks for three-dimensional printing, photosetting-type paints, photosetting ink compositions, nanoparticle inks, inks for ink jet printers, printing screen washing agents, organic semiconductor solutions, inks for color filter production, toners, quinacridone pigment production, succinyl succinate production and dye intermediates; a material or component of oxygen-containing-type diesel fuels and the like; a material or component of cement admixtures, cement treatment agents and the like; a material or component of engine cleaners and the like; a material or component of petroleum refinery solvents and the like; a material or component of oil and natural gas extraction auxiliary agents such as proppant compositions and those auxiliary agents that are used for removal of precipitation filter cakes; a material or component of those products relating to natural gas production, such as natural gas dehydrating solvents; a material or component of construction materials such as low-dust concrete flooring materials and asphalt pavement materials; and a material or component of ink solvents and deinking agents.

DESCRIPTION OF SEQUENCES

-   SEQ ID NO:1 (nucleotide sequence of a primer) -   SEQ ID NO:2 (nucleotide sequence of a primer) -   SEQ ID NO:3 (nucleotide sequence of a primer) -   SEQ ID NO:4 (nucleotide sequence of a primer) -   SEQ ID NO:5 (nucleotide sequence of a primer) -   SEQ ID NO:6 (nucleotide sequence of a primer) -   SEQ ID NOs:7 and 8 (nucleotide sequence of the aroF gene and amino     acid sequence encoded thereby) -   SEQ ID NOs:9 and 10 (nucleotide sequence of the aroG gene and amino     acid sequence encoded thereby) -   SEQ ID NOs:11 and 12 (nucleotide sequence of the aroB gene and amino     acid sequence encoded thereby) -   SEQ ID NOs:13 and 14 (nucleotide sequence of the qsuC gene and amino     acid sequence encoded thereby) -   SEQ ID NOs:15 and 16 (nucleotide sequence of the qsuB gene and amino     acid sequence encoded thereby) -   SEQ ID NOs:17 and 18 (nucleotide sequence of the qsuD gene and amino     acid sequence encoded thereby) -   SEQ ID NO:19 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) -   SEQ ID NO:20 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) -   SEQ ID NO:21 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) -   SEQ ID NO:22 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) -   SEQ ID NO:23 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) -   SEQ ID NO:24 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) -   SEQ ID NO:25 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) -   SEQ ID NO:26 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) -   SEQ ID NO:27 (nucleotide sequence of a polymer used in the     construction of pMJPC17.2) 

The invention claimed is:
 1. A method of producing an organic acid, comprising allowing a microorganism or a treated cell thereof to act on a fermentable sugar, wherein said microorganism has an ability to produce the organic acid and has been modified so that at least one enzyme activity selected from the group consisting of 3-deoxy-D-arabino-heptulosonate-7-phosphate synthase activity, dehydroquinate synthase activity, dehydroquinate dehydratase activity and dehydroshikimate dehydratase activity is reduced as compared to an unmodified strain, and production of an aromatic carboxylic acid is thereby reduced as compared to an unmodified strain.
 2. The method according to claim 1, wherein said microorganism or a treated cell thereof is allowed to act on said organic raw material in an anaerobic atmosphere.
 3. The method according to claim 1, wherein said organic acid is succinic acid.
 4. The method according to claim 1, further comprising the step of performing a crystallization treatment of said organic acid.
 5. The method according to claim 1, wherein said aromatic carboxylic acid is a hydroxybenzene carboxylic acid.
 6. The method according to claim 1, wherein said microorganism is at least one bacterium selected from the group consisting of coryneform bacteria, bacteria belonging to the genus Mycobacterium, bacteria belonging to the genus Rhodococcus, bacteria belonging to the genus Nocardia and bacteria belonging to the genus Streptomyces.
 7. The method according to claim 1, wherein said aromatic carboxlic acid is a protocatechuic acid.
 8. A method of producing a polymer, the method comprising: obtaining the organic acid by the method of claim 1; and polymerizing the organic acid.
 9. The method according to claim 8, wherein said organic acid is subjected to a crystallization treatment.
 10. The method according to claim 8, wherein said aromatic carboxylic acid is a hydroxybenzene carboxylic acid.
 11. The method according to claim 8, wherein said organic acid is succinic acid.
 12. The method according to claim 8, wherein said polymer is a polyester or a polyamide. 